==== Front Sci Rep Sci Rep Scientific Reports 2045-2322 Nature Publishing Group UK London 79018 10.1038/s41598-020-79018-2 Article Broadband dielectric spectroscopy for monitoring temperature-dependent chloride ion motion in BiOCl plates Radoń Adrian adrianr@imn.gliwice.pl 12 Łukowiec Dariusz 2 Włodarczyk Patryk 1 1 grid.425049.e0000 0000 8497 3838Łukasiewicz Research Network - Institute of Non-Ferrous Metals, Sowinskiego 5 St., 44-100 Gliwice, Poland 2 grid.6979.10000 0001 2335 3149Faculty of Mechanical Engineering, Silesian University of Technology, Konarskiego 18 a St., 44-100 Gliwice, Poland 16 12 2020 16 12 2020 2020 10 2209418 8 2020 9 11 2020 © The Author(s) 2020Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.The dielectric properties and electrical conduction mechanism of bismuth oxychloride (BiOCl) plates synthesized using chloramine-T as the chloride ion source were investigated. Thermally-activated structure rebuilding was monitored using broadband dielectric spectroscopy, which showed that the onset temperature of this process was 283 K. This rebuilding was related to the introduction of free chloride ions into [Bi2O2]2+ layers and their growth, which increased the intensity of the (101) diffraction peak. The electrical conductivity and dielectric permittivity were related to the movement of chloride ions between plates (in the low-frequency region), the interplanar motion of Cl− ions at higher frequencies, vibrations of these ions, and charge carrier hopping at frequencies above 10 kHz. The influence of the free chloride ion concentration on the electrical conductivity was also described. Structure rebuilding was associated with a lower concentration of free chloride ions, which significantly decreased the conductivity. According to the analysis, the BiOCl plate conductivity was related to the movement of Cl− ions, not electrons. Subject terms Materials for devicesMaterials for energy and catalysisApplied physicsElectronics, photonics and device physicshttp://dx.doi.org/10.13039/501100007835Politechnika Śląska10/010/BKM20/0378Radoń Adrian issue-copyright-statement© The Author(s) 2020 ==== Body Introduction Oxychlorides have unique properties due to their structure anisotropy. Many different oxychlorides, such as BiOCl, CaOCl2, FeOCl, CuOCl, and ZnOC, have recently been synthesized and tested, especially for use as photocatalysts1–4. Metal oxychloride materials have been investigated because of their chemical stability and their ability to form 2D and 3D nanostructures2,5,6. Interest in the nanostructures of bismuth oxychloride BiOCl is related to their unique optical and electrical properties. Bismuth oxychloride is a semiconductor with a matlockite-type structure with Cl− ions located between [Bi2O2]2+ layers. This structure is responsible for the unique optical, electrical, and catalytic properties of this material. It was confirmed that this charged layered structure can create internal dipole moments7, which is related to the strong intralayer covalent bonding of [Bi2O2]2+ and weak interlayer van der Waals interactions of Cl− double slabs. Moreover, it is possible to create vacancies in the oxychloride structure8,9, which appear in the dielectric spectra and are responsible for the high photocatalytic activity of these materials. BiOCl has been used as a catalyst, especially for the photocatalytic degradation of organic compounds. The influence of shape on the photocatalytic activity of BiOCl for the degradation of toxic bisphenol A was tested for microplates and microflowers, and it was confirmed that the higher adsorption capacity and presence of more active sites in the microflowers enhanced their photocatalytic activity10. Other BiOCl-based nanostructures such as BiOCl/Bi2S3, BiOCl/(BiO)2CO3, and BiOCl/g-C3N4 heterostructures are also good photocatalysts11–13. Due to their potential applications, especially in chloride ion batteries, gas sensors, and supercapacitors, it is important to understand the dielectric properties and electrical conduction mechanism of BiOCl structures over a broad frequency range14–19. The electrical conductivity of BiOCl nanosheets as a function of temperature and oxygen partial pressure was described by Myung et al.20 Their results showed that the band gap of BiOCl nanosheets was 3.34 eV, with a conduction band edge of − 3.36 eV and a valence band edge of − 6.97 eV. They also calculated that the activation energy of conduction below 1000 mbar of oxygen from 300 to 425 K was 862 meV; however, there have been no systematic studies that describe the dielectric properties of BiOCl. Most research has focused on determining its optical and electrical properties, including charge transport in the UV–Vis range8,21–23; therefore, the main goal of recent studies has focused on vacancies and hole-electron generation. Determining charge carrier motion at lower frequencies can broaden the possible applications of oxychloride structures, especially for gas sensors. For example, BiOCl was tested as a gas sensor for CO, CO2, and O2 at 100 kHz by Michel et al.14 who showed that the sensing ability of the sensor was related to electron transport from BiOCl to adsorbed O2. According to this, the number of holes increased in BiOCl, which increased the conductivity. Describing charge carrier transport in BiOCl plates should also clarify the sensing properties at lower frequencies and help correlate the dielectric properties with gas sensing. Describing charge carrier motion in oxychlorides should also extend research on the use of oxychlorides as electrodes, especially in chloride ion batteries. This work focused on describing the dielectric properties and electrical conduction mechanism of BiOCl plates synthesized using chloramine-T as the chloride ion source. Moreover, the influence of structure rebuilding on the structure, conductivity, and chloride ion motion was described using a combination of X-ray diffraction, transmission electron microscopy, and dielectric spectroscopy over broad temperature (173–373 K) and frequency (0.05 Hz–1 MHz) ranges. Experimental section Synthesis of BiOCl plates 10 g of chloramine-T (CH3C6H4SO2NClNa·3H2O) was dissolved in 100 ml of deionized (DI) water. Separately, a solution containing 20 mmol of Bi(NO3)3·5H2O in 50 ml of DI water was prepared. The Bi3+ solution was added into the chloramine-T solution, together with 5 ml of HNO3 (65%). The obtained suspension was heated at reflux for 1 h. Afterward, the suspension was cooled to room temperature and a white precipitated was collected by filtration using quantitative filter paper and then washed with DI water, ethanol, and acetone to remove impurities and water. The synthesized BiOCl was dried at room temperature for 24 h. Characterization of materials The structure rebuilding of BiOCl plates, as well as the structure of as-synthesized plates, were examined using scanning transmission electron microscopy (STEM) and transmission electron microscopy (TEM). The BiOCl dispersion before and after heat treatment was prepared by sonicating a few milligrams of the materials in ultrapure ethanol. The measurements were performed in scanning and transmission modes using an S/TEM TITAN 80-300 according the procedure described before24. The crystal structure of the BiOCl plates was determined using X-ray diffraction (XRD). Powder XRD patterns were recorded using a Rigaku MiniFlex 600 X-ray diffractometer with a copper tube, Cu Kα (λ = 0.15406 nm), a tube voltage of 40 kV, and a current of 15 mA, using a D/teX Ultra silicon strip detector24. The dielectric properties and electrical conduction mechanism were determined using a Concept 81 dielectric spectrometer equipped with an Alpha analyser and a Novo-cool temperature control system. Complex dielectric permittivity and complex conductivity were measured for compressed (pressure = 30 bar) samples in the form of plates with a diameter of 10 mm and a thickness of 1–1.5 mm over a broad frequency range from 0.05 Hz to 1 MHz. To determine the influence of temperature on the dielectric properties, structure rebuilding measurements were conducted in a wide temperature range (173–373 K) with ΔT = 10 K. This procedure was applied in previous works to determine properties of different materials such as ferrites and composites24–26. Results and discussion Structure and morphology The structure and phase purity of as-synthesized BiOCl were examined using XRD. The collected XRD patterns with marked Miller indices (129: P4/nm; DB card number: 1011175) are presented in Fig. 1a. The analysis confirmed that the sample was pure. The high-intensity (001) peak was related to the layered structure, in which covalently-bonded [Bi2O2]2+ layers were separated by chloride ions. To visualize the morphology and structure of BiOCl synthesized using chloramine-T, the STEM and TEM images were analysed. Organic modifiers, chloride ion sources, and reaction conditions (time, temperature, and solvents) play crucial roles in the formation of BiOCl structures with different morphologies27,28. The influence of chloride ion sources on the shape of BiOCl structures was described by Zhao et al.29 Three different types of nanoplate-assembled BiOCl microflowers were synthesized using NaCl, choline chloride, imidazole hydrochloride, and chlorinated pyridine. The representative STEM and TEM images of as-synthesized BiOCl are presented in Fig. 1b–d. As can be seen in Fig. 1b,c , the synthesized material was composed of stacked plates, and the TEM image in Fig. 1d confirms that these plates are composed of many small crystallites with visible boundaries.Figure 1 Structure and morphology of BiOCl plates: (a) XRD pattern of as-synthesized BiOCl using chloramine-T with marked Miller indices for peaks with the highest intensities; (b) HAADF STEM and (c) BF-DF STEM images of BiOCl; (d) TEM image of BiOCl plate with marked planes characteristic of BiOCl; inset shows the SEAD pattern. Dielectric properties To determine dielectric properties and electrical conduction mechanism, dielectric spectra of compressed samples were recorded. As can be seen in Fig. 2a. the value of ε′ increases with increasing temperature up to 283 K. These changes are much more visible in the low-frequency region, which may be related to the space charge polarization at grain boundaries and the accumulation of free charge carriers at the interface between the sample and copper electrode. This behavior is natural and has been observed for various materials, such as ferrites and perovskites25,30. At increasing frequencies, ε′ decreases, which is related to the limited charge carrier movement and the absence of grain boundary polarization; however, during continuous heating up to 373 K, nonlinear changes can be observed (Fig. 2b). After reaching the highest ε′ value at 283 K, the real part of complex permittivity decreases with increasing temperature up to 353 K and then increases again with temperature. This unexpected behavior is likely related to thermally-generated changes in the sample structures. These changes influence the polarization of grain boundaries and the accumulation of free charge carriers. To check the reversibility of this process, the same sample was measured again from 223 to 373 K (sample marked as preheated). As Fig. 2c show, ε′ increases successively with increasing temperature; however, it never reaches the same level as the first measurement, even at higher temperatures. The observed changes can be also presented as ε′ (T) plots for the 1st and 2nd runs (before and after heating) at a constant frequency of 100 Hz (Fig. 2d). During the first heating, a thermally-activated process at Tonset = 283 K can be observed. This nonreversible process is likely related to changes in the number of charge carriers.Figure 2 Dielectric spectra of BiOCl plates: (a) real part of complex permittivity as a function of temperature measured for as-synthesized, compressed sample; (b) real part of complex permittivity as a function of temperature measured in the high-temperature region, with marked nonlinear changes; (c) real part of complex permittivity as a function of temperature measured for preheated BiOCl plates; (d) influence of temperature on the real part of complex permittivity plotted for the sample before (1st run) and after heat treatment (2nd run), with the temperature of the thermally-activated process marked. To confirm this, measurements were repeated for the same compressed sample measured before and after heating. The XRD patterns of these two BiOCl samples (after compressing) are presented in Fig. 3, which shows changes in the intensity of the peaks. For example, the ratio between the intensity of (001) and (101) peaks decreased from 3.15 to 0.86 after heat treatment (Fig. 3a). According to this, the observed nonlinear changes in the dielectric spectra are related to the structure rebuilding.Figure 3 (a) Comparison of XRD patterns of the same BiOCl sample before and after measurements, confirming structure rebuilding [the (*) peak represents the X-ray specimen holder]; (b) visualization of two characteristic planes in the BiOCl unit cell marked on (a): yellow balls represent Bi3+ ions, blue ones O2−, and red ones Cl− ions (CrysTBox cellViewer 1.1331,32); (c) HAADF STEM image of BiOCl plates after compression and heat treatment; (d) TEM image of BiOCl plate after compression and heat treatment with marked planes characteristic of BiOCl; (e) schematic representation of structure rebuilding and influence of this process on chloride ion mobility. The changes in the structure and morphology after heat treatment were presented in the HEEADF STEM and TEM images (Fig. 3c,d). The HAADF STEM image clearly shows that the preheated BiOCl after compression also has a plate-like structure, but some cracks were visible. Therefore any changes generated by the heat treatment are a result of the growth of the crystallites. In the sample before heat treatment, the preferred orientation is a (001) plane in which chloride ions exist between [Bi2O2]2+ layers. These chloride ions are trapped and connected with layers only by van der Waals interactions, therefore they are characterized by the high mobility and can accumulate as free Cl− ions on grain boundaries (Fig. 3e). After heat treatment the preferred orientation is a (101) plane. As can be seen in Fig. 3b, for this plane to be preferred, chloride ions must be incorporated between the [Bi2O2]2+ layers. In order for this process to take place, the rebuilding of the structure has to occur. As presented in Fig. 1d, the as-synthesized BiOCl plates were composed of ultrafine crystallites with a well-formed crystalline structure. After heat treatment, structure rebuilding was also observed in the TEM image. As can be seen in Fig. 3d, the boundaries between well-formed crystallites have disappeared and a homogenous structure was formed. According to that, the increasing intensity of the (101) diffraction peak is related to the incorporation of free chloride ions into positively charged layers, whereas the number of these layers is nearly constant. The mobility of chloride ions is increasing with temperature up to 283 K, at which structure rebuilding occurs. Highly mobile Cl− ions can be “trapped” between [Bi2O2]2+ layers, which changes the crystal structure upon further heating the sample. This process was not observed during the second run, which was associated with the presence of a stable structure in which free Cl− ions did not occur (Fig. 3e). The second useful parameter for describing the motion of charge carriers in inorganic materials is the complex electric modulus, especially its imaginary part. This parameter can describe the transition between the conductivity in grains and by grain boundaries. The complex electric modulus can be expressed as: 1 M∗=M′+iM″=ε′ε∗2+iε″ε∗2 where M′ and M″ are the real and imaginary parts of the complex electric modulus M*, ε′ and ε″ are the real and imaginary parts of the complex permittivity ε*. In the low-temperature region (173–283 K), characteristics of different nonhomogeneous material relationships can be observed: as the temperature increased, the right shoulder of peak M″ shifted to higher frequencies, and the maximum peak was observed at 233 K at 10–1 Hz (Fig. 4a). This peak was previously associated with the transition between long and short-range mobility. Long-range mobility is associated with grain boundaries, whereas short-range mobility is associated with grains; however, the position of this peak differs from other oxides, such as ferrites. The presence of peak M″ at low-frequencies below 1 Hz (region 0) was related to the different conduction mechanisms of oxide-based materials. For oxides and similar materials, the conductivity is related to electron movement, whose movement at grain boundaries occurs even at higher frequencies (sometimes even in the kHz region).Figure 4 (a) Imaginary part of electric modulus M″ for BiOCl before heating at 283 K with marked characteristic regions; (b) imaginary part of electric modulus M″ for BiOCl before heating at high temperatures 293–373 K; (c) imaginary part of electric modulus M″ for preheated BiOCl over a wide temperature range to 373 K with marked characteristic regions; (d) ε″ spectra for BiOCl before (black line) and after heating (red line) with marked regions corresponding to the regions marked in the M″ spectra. The much higher relaxation time expressed as 1/fpeak observed for the BiOCl plates is likely related to the fact that the conductivity of this material does not originate from electrons, but rather from chloride ion movements. These ions are large (167 pm ionic radius); therefore, their movement along grain boundaries is very slow. When the frequency exceeds the maximum of M″, Cl− movement is impossible, and only their slow movement in the crystal structure (between [Bi2O2]2+ layers) was observed (region I + II); however, especially at low temperatures, a second M″ peak was observed (Fig. 4a). As can be seen in Fig. 4a,c, this peak was observed for BiOCl before and after heat treatment (region III). This high-frequency electrical process may be related to the presence of a near-constant loss originating from the vibrations of Cl− ions. Analysis of ε′ showed that when structure rebuilding occurred, the level of free Cl− ions decreased. The same behavior was observed in the M″ (f) plots (Fig. 4b). The M″ peak shifts to lower frequencies at higher temperatures (293–353 K), and then a second shift to higher frequencies was observed (353–373 K). Moreover, the M″ peak disappeared, which proves that there is no transition between long and short-range mobility in the analyzed frequency region. This nonlinear behavior was not observed in the preheated structure. For the stable form of BiOCl, the level of M″ increased with temperature, and three different regions in the M″ spectra were marked. The first one (I) is related to the accumulation of Cl− ions at grain boundaries and at the interface between the sample and copper plate. The second region (II) was related to the electrical process related to interplanar Cl− ion movement, which was also observed in the ε″ spectra (Fig. 4d, red line). As expected, upon increasing the temperature, the chloride ion movement increases and dominates the second process in the higher frequency region. Vibrations of chloride ions and/or polarization of structural defects can also be observed in region III. This process occurs even at high temperatures. According to this, the interplanar movement of Cl− ions at higher frequencies disappears. The same processes were observed for the ε″ spectra at constant temperature and in the materials before and after heating. The value is very high at low frequencies and was associated with Maxwell–Wagner polarization, in which free Cl− ions accumulate at grain boundaries. After heating, this process disappears in the same sample, showing that structure rebuilding occurs. A second peak appeared in the M″ spectra of the preheated sample, which shifted to a higher frequency upon increasing the temperature and peak visible at ε″ spectra were associated with the reorientation of ions (Cl− ions BiOCl). This has been observed for other crystalline ionic materials such as KH2PO4 and CsHSeO433,34 (region II in Fig. 4c). Moreover, this peak not only shifted to higher temperatures but also disappeared with increasing temperatures, and only peak III appeared in the high-temperature region. This peak was not visible for BiOCl before structure rebuilding because the electric processes were dominated by the movements of free chloride ions. A third, rapid process also occurred at high frequencies and low temperatures and was correlated with the presence of oxygen vacancies in BiOCl; therefore, under heating, no additional changes occur during this relaxation process. It was previously reported that BiOCl rich in oxygen vacancies can be synthesized, and the presence of these defects increased the density of states in the valence band maximum35. These oxygen vacancies generate defect dipoles, and the relaxation of these dipoles is visible in the ε″ (f) spectrum. Electrical conductivity The complex electrical conductivity (σ*) (Eqs. 2 and 3) was determined for BiOCl before and after heat treatment. 2 σ∗=ωε″ε0+iωε′ε0 3 σ′=ωε″ε0 According to the analysis, the low-frequency conductivity of as-synthessized and compressed BiOCl plates is likely dominated by the motion of free Cl− ions. After structure rebuilding, the movement of these ions will be limited, and the conductivity mechanism will change. To describe these changes, the real part of electrical conductivity was measured at 253 K, and both cases are presented in Fig. 5a. The conductivity depends on both the frequency and free Cl− ion concentration. The real part of complex electrical conductivity is nearly 100-times higher for the BiOCl structure rich in free Cl− ions (σ′ = 1.4 × 10–12 S/cm at 0.05 Hz) than for the material after rebuilding (σ′ = 9.9 × 10–15 S/cm at 0.05 Hz). The difference between the real part of complex conductivity decreases with increasing frequency. As discussed above, the low-frequency dielectric properties, and also the complex conductivity, are related to chloride ion movement. As the frequency increases, the time for this process is too short; therefore, only interplanar ion movement occurs, and conductivity is related only with electron movement. The interplanar movement of chloride ions most likely allows correlated barrier hopping of electrons between D+ and D− sites. The high-frequency conductivity (near 105 Hz) may be related to electron tunneling or conductivity by holes generated by oxygen vacancies because the Cl− ion movement is impossible in this frequency range, and they can only vibrate. Therefore, the real part of complex conductivity is much higher than in the low-frequency region.Figure 5 (a) Real part of complex conductivity measured for BiOCl before (black points) and after preheating (red points) at 253 K; the influence of temperature on the real part of complex conductivity for BiOCl before (b) and after preheating (c); (d) σ′ (T) relationship measured at 1154 Hz for BiOCl after preheating; σ′ (T) relationship at 0.056 Hz (e) and 1154 Hz (f) for BiOCl before preheating. To confirm this, the influence of temperature on the electrical conductivity was determined, and the measured spectra are presented in Fig. 5b,c. As can be seen in Fig. 5b, the conductivity increases with increasing temperature; however, the temperature did not appear to influence the real part of electrical conductivity for frequencies near 1 MHz. This behavior may be related to the temperature-dependent chloride ion movement in the low-frequency region and temperature non-dependent electrical conductivity by holes or by electron tunneling in the high-frequency region. The possibility of conduction by holes was confirmed by analyzing the M″ spectra, in which a high-frequency electrical modulus peak (marked in region III) may be related to the relaxation of defect dipoles generated by oxygen vacancies. It was previously reported that oxygen vacancies and their defect state provide hopping channels and may be responsible for hole conduction36. The same high-frequency behavior was observed for BiOCl after heat treatment; however, a much lower electrical conductivity was observed even at higher temperatures. Moreover, as can be seen in Fig. 5c, the conductivity increases with increasing temperature; however, for frequencies above 10 Hz, the changes were different than at low frequencies. This unusual behavior is presented in Fig. 5d as σ′ (T) function for the preheated sample. Two different areas were selected: above and below 273 K. First, conductivity increases very rapidly with increasing temperature, followed by a slowdown in this increase and another rapid increase at very high temperatures. This behavior may be related to interplanar Cl− ion movement. The movement of these ions was significantly limited below 273 K, but it increased above this temperature. On the basis of the performed analysis, it can be concluded, that in the low-temperature region the movement of chloride ions can appear only in the crystallites, whereas above the 273 K the mobility of Cl− ion is much higher and the transfer of these ions between crystallites can appear. These changes between short and long-range movements of chloride ions observed in Fig. 5d can be treated as the origin of structure rebuilding. The changes generated by structure rebuilding were also observed in the σ′ (T) spectra and presented for two chosen frequencies in Fig. 5e,f. The conductivity subsequently increases with the increasing temperature up to 293 K (for 0.056 Hz) and up to 283 K (for 1154 Hz). This 10 K difference may be related to the two different conduction mechanisms in the low and high-frequency regions due to Cl− ion movement along grain boundaries and inside the crystalline structure, respectively. Afterward, a rapid decrease in σ′ was observed in both spectra, which was related to structure rebuilding and the temperature-induced movement of chloride ions from the surface of BiOCl plates into the crystal structure. After this process, the conductivity significantly decreased at 0.056 Hz because of the absence of free Cl− ions, which served as charge carriers at this frequency. Much smaller changes were observed at 1154 Hz because at this frequency, the conductivity was related to interplanar Cl− ion movement, which resulted in the correlated barrier hopping of electrons between D+ and D− sites. Therefore, the conductivity was the highest when structure rebuilding occurred (increased movement of chloride ions) and did not decrease to the starting level because a higher Cl− ion concentration in the crystal structure increased the probability of electron hopping. Conclusions BiOCl plates were synthesized using chloramine-T as the chloride ion source. Structure rebuilding at 283 K and the introduction of free Cl− ions into the crystal structure was monitored by changes in broadband dielectric properties and confirmed by XRD patterns and TEM images. Before structure rebuilding, free Cl− ions were responsible for Maxwell–Wagner polarization at low frequencies and high electrical conductivity. The observed M″ behavior confirmed that the electrical conductivity at low frequencies was related to Cl− ion motions, especially free ions (before structure rebuilding) and ions that slowly moved from the crystal structure (after structure rebuilding). After heating above 283 K, structure rebuilding occurred, which decreased the Cl− ion mobility, and thus the conductivity. At higher frequencies, interplanar movement of Cl− ions occurred in the crystal structure, which was responsible for D+ to D− hopping of carriers (probably electrons). This process manifested on ε″ (f) plots and as M″ right shoulder for BiOCl after heat treatment. In this study, the very fast relaxation process represented by the M″ peak in the MHz region was associated with the polarization of structural defects (vacancies) and the movement of holes generated in the material. The high-frequency conductivity (near 105 Hz) may be related to electron tunneling or conductivity by holes generated by oxygen vacancies. This is because the Cl− ion movement cannot occur in this frequency range, and they can only vibrate. The presence of highly mobile free chloride ions at temperatures up to 283 K in the compressed sample is important to construction, especially for efficient chloride ion batteries. Publisher's note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations. Acknowledgements This work was supported by the Silesian University of Technology, Poland [Grant Number 10/010/BKM20/0378]. Author contributions A.R. planned the experiments. A.R. and P.W wrote the main manuscript and performed dielectric studies. D.Ł. performed structural studies. All authors reviewed the manuscript. Competing interests The authors declare no competing interests. ==== Refs References 1. Jones C Ramanathan S Suraneni P Hale WM Calcium oxychloride: a critical review of the literature surrounding the formation, deterioration, testing procedures, and recommended mitigation techniques Cem. Concr. Compos. 2020 10.1016/j.cemconcomp.2020.103663 2. Wu Z Luo W Zhang H Jia Y Strong pyro-catalysis of shape-controllable bismuth oxychloride nanomaterial for wastewater remediation Appl. Surf. Sci. 2020 10.1016/j.apsusc.2020.145630 3. ElMetwally AE Insight into heterogeneous Fenton-sonophotocatalytic degradation of nitrobenzene using metal oxychlorides Sep. Purif. Technol. 2019 10.1016/j.seppur.2018.08.029 4. ElShafei GMS Metal oxychlorides as robust heterogeneous Fenton catalysts for the sonophotocatalytic degradation of 2-nitrophenol Appl. Catal. B Environ. 2018 10.1016/j.apcatb.2017.11.015 5. Chu Y Xing Y Xu HQ Synthesis of samarium oxychloride nanoplates by chemical vapour deposition J. Exp. Nanosci. 2019 10.1080/17458080.2019.1614169 6. Song JM Mao CJ Niu HL Shen YH Zhang SY Hierarchical structured bismuth oxychlorides: self-assembly from nanoplates to nanoflowers via a solvothermal route and their photocatalytic properties CrystEngComm 2010 10.1039/c003497p 7. Li J Yu Y Zhang L Bismuth oxyhalide nanomaterials: Layered structures meet photocatalysis Nanoscale 2014 10.1039/c4nr02553a 25491764 8. Cui D Controlled hydrogenation into defective interlayer bismuth oxychloride via vacancy engineering Commun. Chem. 2020 10.1038/s42004-020-0319-9 9. Cui D Band-gap engineering of BiOCl with oxygen vacancies for efficient photooxidation properties under visible-light irradiation J. Mater. Chem. A 2018 10.1039/c7ta09897a 10. Al Sarihi FTH Marzouqi FA Kuvarega AT Karthikeyan S Selvaraj R Easy conversion of BiOCl plates to flowers like structure to enhance the photocatalytic degradation of endocrine disrupting compounds Mater. Res. Express 2019 10.1088/2053-1591/ab4de0 11. Tanveer M Wu Y Qadeer MA Cao C Atypical BiOCl/Bi2 S3 hetero-structures exhibiting remarkable photo-catalyst response Sci. China Mater. 2018 10.1007/s40843-017-9135-y 12. Al Marzouqi F Controlled microwave-assisted synthesis of the 2D-BiOCl/2D-g-C3 N4 heterostructure for the degradation of amine-based pharmaceuticals under solar light illumination ACS Omega 2019 10.1021/acsomega.8b03665 31459654 13. Chen Y Zhou Y Dong Q Ding H One-step: in situ synthesis of BiOCl/(BiO)2 CO3 composite photocatalysts with exposed high-energy 001 facets CrystEngComm 2018 10.1039/c8ce01608a 14. Michel CR Contreras NLL Martínez-Preciado AH Gas sensing properties of nanostructured bismuth oxychloride Sens. Actuators B Chem. 2011 10.1016/j.snb.2011.07.047 15. Zhao X Zhao-Karger Z Wang D Fichtner M Metal oxychlorides as cathode materials for chloride ion batteries Angew. Chemie Int. Ed. 2013 10.1002/anie.201307314 16. Tan G Zhu X Polyelectrolyte-coated copper hexacyanoferrate and bismuth oxychloride electrodes for efficient salinity gradient energy recovery in capacitive mixing Energy Technol. 2020 10.1002/ente.201900863 17. Tan G Lu S Fan J Li G Zhu X Chloride-ion concentration flow cells for efficient salinity gradient energy recovery with bismuth oxychloride electrodes Electrochim. Acta 2019 10.1016/j.electacta.2019.134724 18. Xia QX Bismuth oxychloride/MXene symmetric supercapacitor with high volumetric energy density Electrochim. Acta 2018 10.1016/j.electacta.2018.03.168 19. Rameshbabu R Sandhiya M Sathish M Fe (III) ions grafted bismuth oxychloride nanosheets for enhanced electrochemical supercapacitor application J. Electroanal. Chem. 2020 10.1016/j.jelechem.2020.113958 20. Myung Y Wu F Banerjee S Park J Banerjee P Electrical conductivity of p-type BiOCl nanosheets Chem. Commun. 2015 10.1039/c4cc09295c 21. Guan M Vacancy associates promoting solar-driven photocatalytic activity of ultrathin bismuth oxychloride nanosheets J. Am. Chem. Soc. 2013 10.1021/ja402956f 24028199 22. Armelao L Bottaro G MacCato C Tondello E Bismuth oxychloride nanoflakes: interplay between composition-structure and optical properties Dalt. Trans. 2012 10.1039/c2dt12098d 23. Liu W-W Peng R-F Recent advances of bismuth oxychloride photocatalytic material: property, preparation and performance enhancement J. Electron. Sci. Technol. 2020 10.1016/j.jnlest.2020.100020 24. Radoń A Łukowiec D Kremzer M Mikuła J Włodarczyk P Electrical conduction mechanism and dielectric properties of spherical shaped Fe3 O4 nanoparticles synthesized by co-precipitation method Mater. (Basel) 2018 10.3390/ma11050735 25. Radoń A Hawełek Ł Łukowiec D Kubacki J Włodarczyk P Dielectric and electromagnetic interference shielding properties of high entropy (Zn, Fe, Ni, Mg, Cd)Fe2 O4 ferrite Sci. Rep. 2019 10.1038/s41598-019-56586-6 31882865 26. Radoń A Włodarczyk P Drygała A Łukowiec D Electrical properties of epoxy nanocomposites containing Fe3 O4 nanoparticles and Fe3 O4 nanoparticles deposited on the surface of electrochemically exfoliated and oxidized graphite Appl. Surf. Sci. 2018 10.1016/j.apsusc.2018.05.045 27. Lei Y Wang G Song S Fan W Zhang H Synthesis, characterization and assembly of BiOCl nanostructure and their photocatalytic properties CrystEngComm 2009 10.1039/b909013b 28. Zhang X Synthesis of a highly efficient BiOCl single-crystal nanodisk photocatalyst with exposing 001 facets ACS Appl. Mater. Interfaces 2014 10.1021/am5010392 25536875 29. Zhao R Li X Zhai Y Li Q Effect of chlorine source on the morphology of flower-like BiOCl and its photocatalytic activity J. Adv. Oxid. Technol. 2015 10.1515/jaots-2015-0223 30. Rayssi C El Kossi S Dhahri J Khirouni K Frequency and temperature-dependence of dielectric permittivity and electric modulus studies of the solid solution Ca0.85 Er0.1 Ti1 − X Co4x/3 O3 (0 ≤ x ≤ 0.1) RSC Adv. 2018 10.1039/c8ra00794b 31. Klinger M Jäger A Crystallographic Tool Box (CrysTBox): automated tools for transmission electron microscopists and crystallographers J. Appl. Crystallogr. 2015 48 2012 2018 10.1107/S1600576715017252 26664349 32. Klinger M More features, more tools, more CrysTBox J. Appl. Crystallogr. 2017 50 1226 1234 10.1107/S1600576717006793 33. Diosa JE Vargas RA Albinsson I Mellander BE Dielectric relaxation of KH2 PO4 above room temperature Phys. Status Solidi Basic Res. 2004 241 1369 1375 10.1002/pssb.200302000 34. Checa O Diosa JE Vargas RA Santamaria J Dielectric relaxation of CsHSeO4 above room temperature Solid State Ionics 2008 180 673 676 10.1016/j.ssi.2009.03.010 35. Cui D Band-gap engineering of BiOCl with oxygen vacancies for efficient photooxidation properties under visible-light irradiation J. Mater. Chem. A 2018 6 2193 2199 10.1039/C7TA09897A 36. Pham HH Wang LW Oxygen vacancy and hole conduction in amorphous TiO2 Phys. Chem. Chem. Phys. 2015 17 541 550 10.1039/C4CP04209C 25406575