==== Front Sci Rep Sci Rep Scientific Reports 2045-2322 Nature Publishing Group UK London 78564 10.1038/s41598-020-78564-z Article Inscribing diffraction grating inside silicon substrate using a subnanosecond laser in one photon absorption wavelength Sugimoto Kozo 1 Matsuo Shigeki matsuos@shibaura-it.ac.jp 1 Naoi Yoshiki 23 1 grid.419152.a0000 0001 0166 4675Department of Mechanical Engineering, Shibaura Institute of Technology, Toyosu, Koto-ku, Tokyo, 135-8548 Japan 2 grid.267335.60000 0001 1092 3579Graduate School of Technology, Industrial and Social Science, Tokushima University, Tokushima, 770-8506 Japan 3 grid.267335.60000 0001 1092 3579Institute of Post-LED Photonics, Tokushima University, Tokushima, 770-8506 Japan 8 12 2020 8 12 2020 2020 10 214511 10 2020 24 11 2020 © The Author(s) 2020Open AccessThis article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.Using focused subnanosecond laser pulses at 1.064μm wavelength, modification of silicon into opaque state was induced. While silicon exhibits one-photon absorption at this wavelength, the modification was induced inside 300μm-thick silicon substrate without damaging top or bottom surfaces. The depth range of the focus position was investigated where inside of the substrate can be modified without damaging the surfaces. Using this technique, diffraction gratings were inscribed inside silicon substrate. Diffraction from the gratings were observed, and the diffraction angle well agreed with the theoretical value. These results demonstrate that this technique could be used for fabricating infrared optical elements in silicon. Subject terms Laser material processingMicro-opticshttp://dx.doi.org/10.13039/501100001691Japan Society for the Promotion of ScienceJP26289019issue-copyright-statement© The Author(s) 2020 ==== Body Introduction In recent years, ultrafast laser processing inside transparent solid materials has been attracting interest as a tool of three-dimensional (3D) micro-nano processing technique1–3. For example, marking, inscribing waveguide, and selective etching inside glass have been reported4–7. In these research, non-linear optical phenomena, such as multi-photon absorption, is utilized for localized modification of materials. Now application fields of ultrafast laser processing inside glass is expanding such as microphotonics and microfluidics1–3. Silicon is one of the most important material in modern technology. Its application field includes large-scale integrated circuits (LSIs), micro-electro-mechanical systems (MEMS) devices, and multi-pixel photodetectors. In these, semiconductor technology based on photolithography, which is a two-dimensional technique, is mainly used for fabrication. Recently research on the use of silicon as a near-infrared (NIR) photonic platform material is active. For such applications, 3D processing using lasers will be advantageous. Silicon is transparent in the near-infrared range (the band gap of silicon is 1.12 eV, and corresponding wavelength is 1.11 μm), thus use of an ultrafast laser in this wavelength range seems promising. However, unlike glasses, difficulty has been reported to process inside silicon with an ultrafast laser in the transparent wavelength region8. Thus, special methods have been executed, such as use of optical setup with extremely high numerical aperture of 2.979, double pulse10, and use of high repetition rate laser11–13. In the study by Matthäus et al.12, waveguides were inscribed in longitudinal geometry starting at the exit surface then moved upstream, in this case the waveguide inscription was significantly facilitated by an imperfectly flat exit surface13. Very recently, it was reported that temporal contrast (pre/post-pulse, pedestal), which is laser technology dependent, of ultrafast laser pulses has a significant effect on the modification threshold energy14. Investigation using THz-repetition-rate pulse bursts also showed the effectiveness of peak-suppressed consecutive pulses for laser modification inside silicon15. In contrast to ultrafast lasers, longer pulse lasers are effective for modification inside silicon. Verburg et al. reported modification inside silicon using laser pulse of 1.549 μm wavelength and 3.5 ns duration16. Tokel et al. used reflection on the back surface and fabricated modification inside silicon with 1.550 μm and 5 ns pulses17. In their method the length of modification along the optical axis was controlled by the number of pulses. They also reported fabrication of waveguide, and selective etching of modified region. Kammer et al. made modifications inside silicon with 1.552 μm wavelength and duration ranging from 800 fs to 10 ps, and reported that 10 ps pulses showed better reproducibility18. Chambonneau et al. fabricated waveguides19 and gratings20 using 1.55 μm wavelength and 5 ns duration pulses, and estimated the degree of refractive index change19,20. Wang et al. inscribed waveguides that have symmetric cross-section in transverse geometry using 1.55 μm wavelength and 3.5 ns duration pulses21. Investigation on pulse-duration dependence was carried out by Das et al., and they reported that pulse duration of 5.4 ps or more is required for making modifications at NA = 0.8522. Generally, one-photon absorption is not used for laser processing inside solid materials. Meanwhile, in cutting silicon substrate using internal modification, a Nd:YAG laser operating at 1.064 μm wavelength is used23, at this wavelength there is weak but non-negligible one-photon absorption (absorption coefficient of silicon at 1.064 μm about 9.7 cm-1 at 295 K)24. However, there have been no report on the use of one-photon absorption based fabrication for optical applications. One-photon absorption based fabrication could be more efficient than that based on multi-photon absorption, whereas there are possible drawbacks that energy loss due to absorption in pre-focal region, and limitation in the inscribing depth due to damaging surface and/or pre-focal region. In addition, a Nd:YAG laser operating at 1.064 μm is widely used. Thus it is worth investigating to apply one-photon absorption based fabrication in modification inside silicon. In this research, we used a subnanosecond Nd:YAG laser operating at 1.064 μm wavelength, and inscribed diffraction gratings inside silicon substrate without damaging top or bottom surfaces. Results and discussion Inscribing inside silicon substrate without damaging surfaces Figure 1 Results of laser-inscribing inside silicon substrate as a function of the position of focus in the sample. (a) scheme of inscribing; all the numbers are in micrometre. The italic numbers shows ascending distance d (see text). Blue rectangle indicates the lines inscribed on the top surface. (b) top view, reflected illumination. (c) Top view, transmitted illumination. (d) Backside view, transmitted illumination. (e) Backside view, reflected illumination. Here, ‘backside view’ indicates that the substrate was inverted and observed from above, and the images were flipped so that the geometry agrees with that of the top views. Figure 2 Pulse energy and scanning speed dependence of modified lines inscribed at d=60 μm. Pulse energy was (a) 8.8 μJ, (b) 6.6 μJ, (c) 4.4 μJ, and (d) 2.2 μJ. In each panel, scanning speed was 30, 50, and 70 μm/s from top to bottom. At first, we examined the condition where we can inscribe modified lines inside silicon substrate without damaging top or bottom surfaces. For this, lines parallel to the surface were inscribed at different depths, experimentally sample position along optical axis was changed for each line, as shown in Fig. 1(a). Hereafter the sample position along optical axis is referred to as ascending distance d; d=0 indicates the focus of laser was set at the top surface of silicon substrate, and positive value of d indicates the sample was moved to the laser source (accordingly, the focus was moved to the bottom surface by roughly d×nSi; nSi is the refractive index of silicon). After inscribing the lines with an objective lens of numerical aperture (NA) = 0.65, the substrate was observed by the NIR microscope under transmitted or reflected illumination. Results with pulse energy of 8.8 μJ and scanning speed of 50 μm/s are shown in Fig. 1(b)–(e). The inscribed lines appeared dark. As seen in the images with transmitted illumination (Fig. 1(c) and (d)), modification (including surface damage) was induced in whole range of d. Surface damages are seen in the images with reflected illumination. As seen in Fig. 1(b) top surface was damaged in d<45 μm, and bottom surface was damaged in d>85 μm as seen in Fig. 1(e). Accordingly, only inside the substrate was modified without damaging top or bottom surfaces in the range about d=45–85 μm. Similar results were obtained with the other pulse energies and scanning speeds. Figure 2 shows pulse energy and scanning speed dependence of modified lines at d=60 μm, where the lines were inscribed without damaging surfaces with all parameters shown here. The thickness of the lines was in the range of 2–6 μm depending on the pulse energy and scanning speed. The higher pulse energy or the slower scanning speed, the thicker the lines. In addition, some of the lines had irregularity in width.Figure 3 (a) Optical micrograph of cleaved face of silicon substrate. The substrate was cleaved perpendicular to the laser-inscribed lines. (b) Micro-Raman spectra of modified and un-modified spots around 520 cm-1. Three solid curves are spectra from modified spots, and three dashed curves are spectra from un-modified spots. Characterization of modification inside silicon substrate Cross-section of silicon substrate with inscribed lines was observed. The irradiation condition was the same as that in Fig. 1 (8.8 μJ, 50 μm/s), and d was set at 52 μm. The substrate was cleaved perpendicular to the inscribed lines, As seen in Fig. 3(a), a series of modified spots aligned in vertical direction (that is, the direction of laser irradiation) is observed. The presence of the vertically aligned spots indicates that completely 3D-localized modification was not realized yet, but the modification was localized in two-dimensions thus can be used in two-dimensional applications. Such a series of modified spots have been reported in nanosecond laser processing of silicon25,26. In these studies, modified spots were identified as voids. Li et al. explained that this phenomena is due to void formation and hydrodynamic phenomena occurring near the void induced by successive laser pulses25. We presume that similar phenomenon occurred in our case, while laser wavelength was different. Another possibility might be a phenomena related to the propagation of the absorption front to the upstream of the incoming laser27,28. In this case, however, the speed of propagation is about 1 μm /1 ns or less, thus it is difficult to explain the total length of the observed modified spots considering the pulse duration of 0.5 ns in the present study. In order to elucidate the nature of modified spots, micro-Raman spectra were measured at modified and un-modified spots (three spots each) on the cleaved face. Figure 3(b) shows the spectra around 520 cm-1. Compared to the spectra from un-modified spots, the spectra from modified spots are broader and shifted to lower Raman shift. These changes can be explained by polycrystallization29,30 or strain31,32. Grating and diffraction Several gratings with different period and width of lines were inscribed. Pulse energy was 8.8 μJ, scanning speed was 50 μm/s, and d was 60 μm for all. Figure 4 shows one of the gratings observed with the NIR microscope transmitted illumination. Here 11 dark lines were inscribed with a lattice constant of 34 μm. The width of the dark lines were about 24 μm; each line consists of six paths of inscription with a separation of 4 μm. As seen in Fig. 4, grating was inscribed inside silicon substrate as designed. In addition, this transmitted illumination image indicates that the inscribed grating is, at least in part, an amplitude grating, whereas Chambonneau et al. evaluated only the real part of the refractive index change in the laser-modified zone20. Diffraction pattern from the gratings were observed in transmission geometry. Figure 5(a) shows the diffraction pattern from the grating of Fig. 4. The distance between the grating and the target paper was set at L=150 mm. As seen, in addition to the strong zero-order line, diffraction lines up to 4-th order were observed. In this case, theoretically, first-order diffraction should be found at ±4.7 mm (=Ltanθ, where θ=sin-1(λ/Λ) is the first-order diffraction angle, λ is the laser wavelength, and Λ is the lattice constant). The experimental result is in good agreement with the theoretical one. Dependence of first-order diffraction angle on the lattice constant is shown in Fig. 5(b). As seen, diffraction angle from the other gratings also agreed with the theory well. These results indicate that the fabricated gratings inside silicon substrate functioned as expected.Figure 4 Grating inscribed inside silicon substrate (top view, transmitted illumination). Figure 5 (a) Diffraction pattern from the grating in Fig. 4. The distance between the grating and the target paper was 150 mm. The dark lines in the image are the marks written on the target paper (see Methods). (b) Dependence of first-order diffraction angle on the lattice constant. The width of the dark lines was varied, so that the width of the transparent lines was kept constant at 10 μm. Conclusion We have inscribed diffraction gratings inside 300 μm-thick silicon substrate using a subnanosecond laser of 1.064 μm wavelength. Although silicon exhibits non-negligible one-photon absorption at this wavelength, the gratings were inscribed without damaging top or bottom surfaces. The functionality of the inscribed gratings were demonstrated. So far, internal modification inside silicon substrate by laser pulse of 1.064 μm wavelength has been used for dicing. The present results indicate that the modification based on one-photon absorption can also be used for optical applications. Silicon is one of important infrared optical materials. This technique would be useful for fabricating amplitude optical elements in silicon. Methods N-type Si (100) substrates with a thickness of 0.3 mm, mirror-polished on both sides, were cut into 10 mm×8 mm pieces, and used for experiments. The light source used for laser-inscribing was a subnanosecond Nd:YAG laser (PNP-M08010-130, Teem Photonics) with a wavelength of 1.064 μm and a pulse duration of 0.5 ns. There are no pre-pulses or pedestals, and there could be post-pulses with a contrast of 1:10 (post-pulse:main-pulse energy). The repetition rate was 100 Hz for all the experiments shown in this article. The laser beam was led to a near-infrared (NIR) upright optical microscope (BX-51, Olympus), and focused by an objective lens with correction collar (LCPLN50XIR, Olympus, numerical aperture (NA) = 0.65) from the top. The theoretical spot size is 1.22λ/NA=2.0 μm. The correction collar settings was fixed to 0.3; this value was chosen because empirically it gives a reasonable focus on all range of depth. The laser pulse energy was measured at a fixed point in front of the microscope and multiplied by the overall transmission. The sample was placed on a three-axis motorized stage (MMU-60X·Y and ALZ-6012-G0M, Chuo Precision Industrial) and moved along the pre-programmed pattern.Figure 6 The mark printed on the target paper. The blue-dashed rectangle approximately indicates the region shown in Fig. 5. To observe the laser inscribed lines inside the substrate, a NIR camera (CONTOUR-IR digital, Electrooptic) was attached on the same microscope, and observed under transmitted or reflected illumination. Under transmitted illumination the dark (opaque) region in whole thickness of the substrate was observed, while under reflected illumination only the top surface was observed. In both transmitted/reflected illumination, the light source was a halogen lamp (U-LH100IR, Olympus). A confocal Raman microscope (LabRAM HR Evolution, Horiba) was used for measuring Micro-Raman spectra. For the observation of diffraction pattern from the fabricated gratings, non-focused laser beam at 1.064 μm wavelength was irradiated to the grating at normal incidence, and the pattern of transmitted (diffracted) light on a target paper was recorded by a digital camera (E-PM2, Olympus). The camera has week sensitivity at 1.064 μm; laser beam appeared violet in the recorded images. Because of the observation angle, the image was slightly distorted. Thus, a cross mark and concentric circles were printed on the target paper as show in Fig. 6. Publisher's note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations. Acknowledgements This work was partly supported by JSPS KAKENHI Grant Number JP26289019. Author contributions S.M. and Y.N. designed the research. K.S. conducted the experiments, K.S. and S.M. analysed the results. All authors reviewed the manuscript. Competing interests The authors declare no competing interests. ==== Refs References 1. Gattass RR Mazur E Femtosecond laser micromachining in transparent materials Nat. Photon. 2008 2 219 225 10.1038/nphoton.2008.47 2. Osellame R Hoekstra H Cerullo G Pollnau M Femtosecond laser microstructuring: An enabling tool for optofluidic lab-on-chips Laser Photon. Rev. 2011 5 442 463 10.1002/lpor.201000031 3. Sugioka K Cheng Y Femtosecond laser three-dimensional micro- and nanofabrication Appl. Phys. Rev. 2014 1 041303 10.1063/1.4904320 4. Glezer EN 3-D optical storage inside transparent materials Opt. Lett. 1996 21 2023 2025 10.1364/OL.21.002023 19881880 5. Davis KM Miura K Sugimoto N Hirao K Writing waveguides in glass with a femtosecond laser Opt. Lett. 1996 21 1729 1731 10.1364/OL.21.001729 19881782 6. Kondo Y Qiu J Mitsuyu T Hirao K Yoko T Three-dimensional microdrilling of glass by multiphoton process and chemical etching Jpn. J. Appl. Phys. 1999 38 L1146 L1148 10.1143/JJAP.38.L1146 7. Marcinkevičius A Femtosecond laser-assisted three-dimensional microfabrication in silica Opt. Lett. 2001 26 277 279 10.1364/OL.26.000277 18040300 8. Mouskeftaras A Self-limited underdense microplasmas in bulk silicon induced by ultrashort laser pulses Appl. Phys. Lett. 2014 105 191103 10.1063/1.4901528 9. Chanal M Crossing the threshold of ultrafast laser writing in bulk silicon Nat. Commun. 2017 8 773 10.1038/s41467-017-00907-8 28974678 10. Mori M Tailoring thermoelectric properties of nanostructured crystal silicon fabricated by infrared femtosecond laser direct writing Phys. Status Solidi (a) 2015 212 715 721 10.1002/pssa.201431777 11. Pavlov I Femtosecond laser written waveguides deep inside silicon Opt. Lett. 2017 42 3028 10.1364/OL.42.003028 28957237 12. Matthäus G Inscription of silicon waveguides using picosecond pulses Opt. Express 2018 26 24089 10.1364/OE.26.024089 30184901 13. Alberucci A In-depth optical characterization of femtosecond-written waveguides in silicon Phys. Rev. Appl. 2020 14 024078 10.1103/PhysRevApplied.14.024078 14. Wang A Das A Grojo D Temporal-contrast imperfections as drivers for ultrafast laser modifications in bulk silicon Phys. Rev. Res. 2020 2 033023 10.1103/PhysRevResearch.2.033023 15. Wang A Das A Grojo D Ultrafast laser writing deep inside silicon with THz-repetition-rate trains of pulses Research 2020 2020 1 11 10.34133/2020/8149764 16. Verburg PC Römer GRBE Huis Int Veld AJ Two-photon-induced internal modification of silicon by erbium-doped fiber laser Op. Express 2014 22 21958 71 10.1364/OE.22.021958 17. Tokel O In-chip microstructures and photonic devices fabricated by nonlinear laser lithography deep inside silicon Nat. Photonics 2017 11 639 645 10.1038/s41566-017-0004-4 28983323 18. Kämmer H In-volume structuring of silicon using picosecond laser pulses Appl. Phys. A 2018 124 302 10.1007/s00339-018-1715-1 19. Chambonneau M Li Q Chanal M Sanner N Grojo D Writing waveguides inside monolithic crystalline silicon with nanosecond laser pulses Opt. Lett. 2016 41 4875 10.1364/OL.41.004875 27805639 20. Chambonneau M Richter D Nolte S Grojo D Inscribing diffraction gratings in bulk silicon with nanosecond laser pulses Opt. Lett. 2018 43 6069 10.1364/OL.43.006069 30548006 21. Wang X Nanosecond laser writing of straight and curved waveguides in silicon with shaped beams J. Laser Appl. 2020 32 022002 10.2351/1.5139973 22. Das A Wang A Uteza O Grojo D Pulse-duration dependence of laser-induced modifications inside silicon Opt. Express 2020 28 26623 10.1364/OE.398984 32906932 23. Kumagai M Advanced dicing technology for semiconductor wafer-stealth dicing IEEE Trans. Semicond. Manuf. 2007 20 259 265 10.1109/TSM.2007.901849 24. Schinke C Uncertainty analysis for the coefficient of band-to-band absorption of crystalline silicon AIP Adv. 2015 5 067168 10.1063/1.4923379 25. Li Q Chambonneau M Chanal M Grojo D Quantitative-phase microscopy of nanosecond laser-induced micro-modifications inside silicon Appl. Opt. 2016 55 9577 10.1364/AO.55.009577 27869860 26. Iwata H Kawaguchi D Saka H Electron microscopy of voids in Si formed by permeable pulse laser irradiation J. Electron Microsc. 2017 66 328 336 10.1093/jmicro/dfx024 27. Ohmura E Fukuyo F Internal modified-layer formation mechanism into silicon with nanosecond laser J. Achieve. Mater. Manuf. Eng. 2006 17 381 384 28. Kiyota H Hara K Jankowski M Fejer MM Numerical simulation and validation of subsurface modification and crack formation induced by nanosecond-pulsed laser processing in monocrystalline silicon J. Appl. Phys. 2020 127 085106 10.1063/1.5130701 29. Richter H Wang Z Ley L The one phonon Raman spectrum in microcrystalline silicon Solid State Commun. 1981 39 625 629 10.1016/0038-1098(81)90337-9 30. Shabir Q Medically biodegradable hydrogenated amorphous silicon microspheres Silicon 2011 3 173 176 10.1007/s12633-011-9097-4 31. Wolf ID Micro-Raman spectroscopy to study local mechanical stress in silicon integrated circuits Semicond. Sci. Technol. 1996 11 139 154 10.1088/0268-1242/11/2/001 32. Kämmer H Origin of waveguiding in ultrashort pulse structured silicon Laser Photon. Rev. 2019 13 1800268 10.1002/lpor.201800268