==== Front Nanomaterials (Basel) Nanomaterials (Basel) nanomaterials Nanomaterials 2079-4991 MDPI 32344874 10.3390/nano10050821 nanomaterials-10-00821 Article Various Coating Methodologies of WO3 According to the Purpose for Electrochromic Devices Kim Keon-Woo 1† https://orcid.org/0000-0002-0010-0883Kim Yong Min 2† Li Xinlin 3 Ha Taehwa 1 https://orcid.org/0000-0001-7818-1903Kim Se Hyun 1* Moon Hong Chul 2* https://orcid.org/0000-0001-7523-5371Lee Seung Woo 1* 1 School of Chemical Engineering, Yeungnam University, 280 Daehak-ro, Gyeongsan 38541, Korea 2 Department of Chemical Engineering, University of Seoul, Seoul 02504, Korea 3 College of Electromechanical Engineering, Qingdao University, Qingdao 266071, China * Correspondence: shkim97@yu.ac.kr (S.H.K.); hcmoon@uos.ac.kr (H.C.M.); leesw1212@ynu.ac.kr (S.W.L.)† These authors contributed equally to this work. 25 4 2020 5 2020 10 5 82119 3 2020 24 4 2020 © 2020 by the authors.2020Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/).Solution-processable electrochromic (EC) materials have been investigated widely for various applications, such as smart windows, reflective displays, and sensors. Among them, tungsten trioxide (WO3) is an attractive material because it can form a film via a solution process and relative low temperature treatment, which is suitable for a range of substrates. This paper introduces the slot-die and electrostatic force-assisted dispensing (EFAD) printing for solution-processable methods of WO3 film fabrication. The resulting films were compared with WO3 films prepared by spin coating. Both films exhibited a similar morphology and crystalline structure. Furthermore, three different processed WO3 film-based electrochromic devices (ECDs) were prepared and exhibited similar device behaviors. In addition, large area (100 cm2) and patterned ECDs were fabricated using slot-die and EFAD printing. Consequently, slot-die and EFAD printing can be used to commercialize WO3 based-ECDs applications, such as smart windows and reflective displays. electrochromic devicetungsten trioxideprinted electronicsslot-dieelectrohydrodynamic jet printing ==== Body 1. Introduction Solution-processable electronic materials have attracted considerable attention in a range of optoelectronic fields, such as displays [1,2,3], thin-film transistors [4,5,6], and sensors [7,8,9]. This is because their processing advantages (e.g., roll-to-roll [10,11,12] and several printing processes [13,14,15,16]) make it possible to commercialize low-cost and large-area optoelectronic devices. Among them, electrochromic (EC) materials (e.g., metal oxides [3,9,13], metal complexes [17,18], viologens [19,20,21,22,23,24,25], small organic molecules [26,27], metallo-supramolecular polymers [28,29,30,31], and conducting polymer thin films [32,33,34,35]) exhibit a reversible change in optical transmittance in response to an applied external voltage. Therefore, they have been investigated extensively for use in a variety of applications, such as reflective displays, antiglare mirrors, smart windows, and functional supercapacitors. Tungsten trioxide (WO3) is a widely used EC material owing to its facile fabrication method via solution processing, such as a sol-gel technique at relatively low temperatures (~60 °C), which enables the use of conventional plastic substrates including polyethylene terephthaltate (PET) [3,13,36]. To apply WO3 in information displays or smart mirror/windows, it is necessary to develop manufacturing techniques to suit the characteristics of the application. Although spin-casting is one representative method to form WO3 films and investigate various EC properties in detail [36], there are demands to make shapes or letters for information transfer (display application). In addition, the previous methods may not be efficient for large area manufacturing with respect to film uniformity and quantity of materials consumption during film formation (smart window/mirror application). Therefore, an appropriate methodology is needed to commercialize WO3-based EC device (ECD) applications. This paper introduces slot-die coating and electrohydrodynamic (EHD) jet printing of a WO3 ink for a uniform film coating on a large area and patterning, respectively. A slot-die coating method allows the pre-metered and continuous coating of ink flowing from the downstream meniscus, forming at a horizontal slot-die head edge while the ink is supplied consistently in the slot-die head [15,37]. Therefore, it is considered to be a cost-effective and easily scalable technique for the high throughput and large area film production field [38,39,40]. On the other hand, EHD jet printing enables uniform and continuous line patterning by forming a jet stream from the nozzle tip, where the electrostatic force applied between a nozzle tip and a substrate can deform the meniscus of an ink to eject droplets consistently [11,13,14]. Among EHD printing modes, electrostatic force-assisted dispensing (EFAD) mode, which applies very low external voltage between the nozzle tip and substrate for the formation of continuous ink flow between the two, have been frequently applied to make patterns for electronic materials with good pattern fidelity and morphological uniformity [36]. In this study, the coating and morphological properties of WO3 films fabricated by slot-die coating and EFAD printing were characterized and compared with films produced by spin-coating. In addition, the EC performance of the device fabricated by each printing method was compared. The ECDs showed similar morphological properties of WO3 and device behaviors, such as optical modulation, switching speed, and coloration efficiency. These results imply that the slot-die and EFAD printing can be commercialized for diverse WO3-based ECDs applications. To demonstrate the feasibility, the large scale (100 cm2) and patterned WO3-based ECDs were produced by slot-die and EFAD printing, respectively. The obtained ECDs can be used as smart windows and reflective display applications. 2. Materials and Methods 2.1. Materials Except for ITO glass (sheet resistance: 15 Ω/sq, Asahi Glass Co., Tokyo, Japan), all materials were purchased from Sigma-Aldrich (St. Louis, MO, USA). Tungsten trioxide (WO3) nanoparticles were prepared using a method reported elsewhere [3,13,14,32]. To synthesize WO3 nanoparticles, tungsten (W) powder (7.0 g) was added to hydrogen peroxide solution (31 wt.% in water, 90 g) and allowed to react at 100 °C. After 5 h, the solvent was evaporated by using rotary evaporator, giving WO3 nanoparticles. The characterizations of resulting WO3 nanoparticles using photograph, scanning electron microscopy (SEM) and X-ray diffraction (XRD) are shown in Figure S1a–c, respectively. A WO3 suspension was fabricated by mixing WO3 nanoparticles, DI-water, and isopropyl alcohol (IPA) at a weight ratio of 0.3:0.35:0.35, respectively, followed by sonication for 4 h to obtain a homogeneous dispersion. Before WO3 suspension deposition, ITO glasses were cleaned sequentially with acetone (15 min) and IPA (15 min) with sonication, and a UV/ozone treatment was then conducted for 10 min prior use. In addition, propylene carbonate containing LiClO4 (0.5 M) and ferrocene (0.05 M) was used as an electrolyte. 2.2. Fabrication of Tungsten Oxide Film In this study, three different processes (spin coating, slot-die, and EFAD printing) were used to fabricate WO3 films, and the thickness of the WO3 films was maintained for a fair comparison. To fabricate the same film thickness, in the case of spin coating, the WO3 suspension was spin-coated on ITO at 5000 rpm for 20 s. For the slot-die process, a WO3 suspension was ejected into the slot-die head at a flow rate of 1 mL/min, and the moving speed was set to 5 mm/s. In EFAD printing, the flow rate of the WO3 suspension was fixed to 0.5 µL/min, and the applied voltage between the nozzle tip and substrate and printing velocity were 10 V and 3 mm/s, respectively. To prepare WO3 films with a size of 1.5 cm × 1.5 cm using spin-coating, slot-die and EFAD printing, the WO3 suspension required approximately 100 µL, 1 µL and 1 µL, respectively. Prior to use, the as-spun WO3 films were annealed thermally at 60 °C under vacuum for 10 h. 2.3. Device Fabrication and Characterization The WO3 films obtained by the three different processes were characterized by optical microscopy (OM, ECLIPSE LV100ND, Nikon, Tokyo, Japan), scanning electron microscopy (SEM, S-4800, Hitachi, Tokyo, Japan), X-ray diffraction (XRD, D/MAX2500 VL-PC, Rigaku, Tokyo, Japan), and cyclic voltammetry (Weis 500, WonA Tech., Seoul, Korea). For WO3-based ECDs assembly, the WO3-coated ITO glass, electrolyte solution, and counter bare ITO glass were sandwiched to form the (ITO/WO3/electrolyte/ITO) configuration, in which ~88 µm thick double-sided tape was used as a spacer and adhesive. To investigate the performance of ECDs, DC and square-shaped wave voltages were supplied by a potentiostat (Wave Driver 10, Pine Instrument, Durham, NC, USA). In addition, a UV–VIS spectrophotometer (V-730, Jasco, Easton, MD, USA) was used to record the change in transmittance according to the applied voltages. All ECDs in this work were fabricated to a size of 1.5 cm × 1.5 cm to measure characteristics. 3. Results Figure 1 presents the WO3-based ECD configuration and schematic descriptions of various WO3 deposition processes (spin coating, slot-die, and EFAD printing) in this study. EC devices based on WO3-coated ITO glass were fabricated using propylene carbonate (PC) as an electrolyte containing 0.5 M LiClO4 and 0.05 M ferrocene (Fc) (Figure 1a). In this device, the ion storage layer was unnecessary because Fc acted as anodic species. Thus, the device configuration became simple. In the spin-coating process (Figure 1b), the ITO glass should be fixed on a vacuum chamber, followed by casting the WO3 suspension on ITO glass and spinning the chamber to form a uniform WO3 film. Although spin coating is a facile method to fabricate the films precisely, it is limited to large area and patterning productions because of the necessity of large amounts of solution and additional post-process. The slot-die and EFAD printing are attractive technologies that allow the fabrication of large area and patterned films by the simple direct printing of a solution. Figure 1c,d show schematic illustrations of the slot-die and EFAD printing processes, respectively. The slot-die head was placed vertically at ITO glass, and the WO3 suspension was injected through a connected tube. The WO3 suspension was ejected from slot-die head to ITO glass, while the slot-die head was moved horizontally to form a uniform large-area WO3 film. In EFAD printing, the WO3 suspension was filled into a syringe with a nozzle. An electric field between the nozzle tip and ITO glass was applied to enable well-defined and continuous line printing while moving the sample stage. The three different films (obtained by spin coating, slot-die, and EFAD printing) underwent thermal annealing at 60 °C under vacuum prior to use. The WO3 film morphologies obtained by three different processes were investigated by OM, as shown in Figure 2a–c (see the SEM images in the inset). The thickness of three WO3 films were determined to be ~300 nm (see cross-section SEM images in Figure S2). OM showed that all the films except for the EFAD film exhibited a similar shape. The EFAD film showed an overlapped line pattern because it needed to be printed several times to produce the same film thickness as the spin-coating and slot-die films. Although the OM image of the EFAD film showed an overlapping line pattern, SEM revealed the three different films to have a similar morphology. Specifically, electrochromic performance is governed by the crystalline structure of WO3. Therefore, the crystalline structure of the WO3 films (spin coating, slot-die, and EFAD) was examined by XRD. Figure 2d shows the XRD patterns of the WO3 films before and after thermal annealing. The as-spun WO3 film (before thermal annealing) showed XRD reflections corresponding to the (002), (200), and (202) planes. After thermal annealing, each WO3 film (spin coating, slot-die, and EFAD) exhibited an enhanced (002) peak intensity, indicating the development of the monoclinic crystalline structure of WO3. Therefore, the electrochromic (EC) performance of each WO3 film-based ECD was expected to be similar because of their comparable film morphology and crystalline structure. The cyclic voltammograms (CVs) of WO3-coated films fabricated by three different methods were recorded at a scan rate of 25 mV/s from +1.0 to −1.5 V to estimate the electrochemical properties and electrochromic performances of the films (Figure S3). When applied to a negative potential, significant increasing current densities were measured at each film indicating an activation process for the intercalation of Li+ ions into the films. Despite the different coating methods, the shapes of the CV curves were similar for all the coating methods. To examine the EC behaviors of the three different WO3 film-based ECDs, the transmittance variations, according to the applied voltage, were recorded at 350–900 nm (Figure 3a–c). A noticeable decrease in the transmittance spectra was observed at −0.3 V, and the transmittance spectra of ECDs according to applied voltage exhibited similar behavior. The color changes at increasing bias were also analyzed with CIELAB color coordinates. In the bleached state the films had a slight yellowish color with L*, a* and b* of each device are (72.26, 7.67, 16.8), (76.72, 6.24, 8.95), and (71.33, 7.68, 15.21) for spin-coated, slot-die coated, and EFAD films (Figure S4a–c). When increasing the applied voltage until −1.5 V, the devices become blue with the similar values of L*, a* and b*. In addition, the transmittance variations at 700 nm of the three different WO3 film-based ECDs as a function of the applied voltage were derived (Figure 3d). As the applied voltage was increased, the transmittance decreased, and ΔT of the three different WO3 film-based ECDs were similar 71.3%, 72.8%, and 72.1% at −1.5 V, respectively. The optical transitions of each ECD were also observed clearly, as shown in Figure 3e. The EFAD film-based ECD showed slightly different dynamic behavior compared to the spin coating and slot-die film based ECDs. To measure the dynamic device behavior, the transmittance profiles of the ECDs were recorded at 700 nm upon the application of −1.5 V (coloration) and 0 V (bleaching) (Figure 4). The response times of coloration (tc) and bleaching (tb) were defined as the times at which 90% of the maximum transmittance contrast (ΔT) was achieved. The similar coloration (tc) and bleaching (tb) times were obtained as tc = ~14 s and tb = ~10 s (spin-coating), tc = ~12 s and tb = 8.5 s (slot-die) and tc = ~12 s and tb = 9 s (EFAD printing). To examine the coloration efficiency (η) of the three different ECDs, the correlation between the optical density (OD) and charge density (Q) was plotted, as shown in Figure 5. The η value, which is defined as ΔOD/ΔQ, corresponds to the slope of the linear fit in the linear regime. The similar η values of each ECD were recorded as ~40.2 (spin-coating), ~38.5 (slot-die), and ~41.0 cm2/C (EFAD printing). By applying the advantages of slot-die and EFAD printing, which can print a WO3 suspension on a large and selective area, large area (100 cm2) and patterned WO3-based ECDs were obtained, as shown in Figure 6. The color of the large area WO3-based ECD changed reversibly over the entire area when the bleached state and colored state were observed at 0 V and −1.5 V, respectively (Figure 6a). Reversible EC behavior was observed in the line patterned WO3-based ECD (Figure 6b). In addition, electrochromic letters (YU) were produced using the EFAD printing method (Figure 6c). Accordingly, slot-die and EFAD printing can be used to commercialize WO3-based ECD applications, such as smart windows and reflective displays. 4. Conclusions WO3-based ECDs were fabricated by spin coating, slot-die, and EFAD printing techniques. The morphology of the WO3 films obtained by the above three processes showed a similar shape, except for the EFAD film, which showed an overlapping line. Although the EFAD film exhibited a different morphology, the crystalline structure was no different compared to spin coating and slot-die, which has a monoclinic structure. In addition, the device performance of three different WO3-based ECDs was similar. For example, each WO3-based ECD produced from spin-coating, slot-die, and EFAD printing showed similar optical modulation (~71.3%, ~72.8%, and ~72.1%), response times (tc = ~14, ~12, ~12 s), and coloration efficiencies (~40.2, ~38.5, ~41.0 cm2/C). Large area (100 cm2) and patterned WO3 electrochromic devices were demonstrated by taking advantage of the slot-die and EFAD printing processing methods. Slot-die and EFAD printing are attractive technologies for commercializing WO3-based ECDs into smart windows and reflective displays. Supplementary Materials The following are available online at https://www.mdpi.com/2079-4991/10/5/821/s1, Figure S1: Information of the WO3 nanoparticles; Figure S2: Cross-section SEM images of WO3 films; Figure S3: Cyclic voltammograms (CVs) of WO3 films; Figure S4: Variations in CIELAB color coordinates of the WO3-based ECDs. Click here for additional data file. Author Contributions K.-W.K. and Y.M.K. contributed equally to this work. Conceptualization: Y.M.K., S.H.K. and H.C.M.; methodology: K.-W.K. and S.W.L.; validation: K.-W.K., Y.M.K., X.L., T.H., S.H.K. and H.C.M.; formal analysis: Y.M.K.; investigation: K.-W.K.; writing—original draft preparation: K.-W.K., Y.M.K. and H.C.M.; writing—review and editing: S.H.K. and S.W.L.; funding acquisition: S.W.L., H.C.M. and S.H.K. All authors have read and agreed to the published version of the manuscript. Funding This study was supported by the Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Education, Science and Technology (NRF-2019R1A2C1004499) and “Human Resources Program in Energy Technology” of the Korea Institute of Energy Technology Evaluation and Planning (KETEP), granted financial resource from the Ministry of Trade, Industry and Energy, Republic of Korea (no. 20174030201760). This work was partly supported by Korea Institute of Energy Technology Evaluation and Planning (KETEP) grant funded by the Korea government (MOTIE) (20193020010370). Conflicts of Interest The authors declare no conflict of interest. Figure 1 (a) Device configuration of the electrochromic device (ECD) in this study. Schematic illustrations of the WO3 film fabrication processes in this study (b) spin coating, (c) slot-die, and (d) electrostatic force-assisted dispensing (EFAD) printing. Figure 2 Optical microscopy (OM) and scanning electron microscopy (SEM) (see in inset) images of WO3 films morphology obtained by (a) spin-coating, (b) slot-die and (c) EFAD printing. (d) X-ray diffraction (XRD) patterns of the WO3 films, as-spun, and after thermal annealing at 60 °C under vacuum. Figure 3 Variation in the UV–VIS spectra for ECDs obtained by three different processes (a) spin-coating, (b) slot-die, and (c) EFAD printing. (d) Voltage dependence of the transmittance at 700 nm. (e) Photograph of the original state (no bias), colored state (−1.5 V), and bleached state (0 V). The scale bar represents 20 mm. Figure 4 Transmittance profile at 700 nm for ECDs fabricated by three different processes upon the application of −1.5 V (coloration) and 0 V (bleaching). Figure 5 Plots of the optical density as a function of the charge density for three different processes ECDs (a) spin-coating, (b) slot-die, and (c) EFAD printing. Figure 6 Photographs of the bleached and colored states of WO3-based ECDs fabricated by (a) slot-die and (b,c) EFAD printing. ==== Refs References 1. Ricciardulli A.G. Blom P.W.M. Solution-Processable 2D Materials Applied in Light-Emitting Diodes and Solar Cells Adv. Mater. Technol. 2020 1900972 10.1002/admt.201900972 2. Duan L. Hou L. Lee T.-W. Qiao J. Zhang D. Dong G. Wang L. Qiu Y. Solution Processable Small Molecules for Organic Light-Emitting Diodes J. Mater. Chem. 2010 20 6392 6407 10.1039/b926348a 3. Zhong C. Duan C. Huang F. Wu H. Cao Y. Materials and Devices toward Fully Solution Processable Organic Light-Emitting Diodes Chem. Mater. 2011 23 326 340 10.1021/cm101937p 4. Gong Y. Zhao K. He H. Cai W. Tang N. Ning H. Wu S. Gao J. Zhou G. Lu X. Solution Processable High Quality ZrO2 Dielectric films for Low Operation Voltage and Flexible Organic Thin Film Transistor Applications J. Phy. D Appl. Phys. 2018 51 115105 10.1088/1361-6463/aaac1b 5. Rullyani C. Sung C.-F. Lin H.-C. Chu C.-W. Flexible Organic Thin Film Transistors Incorporating a Biodegradable CO2 -Based Polymer as the Substrate and Dielectric Material Sci. Rep. 2018 8 8146 10.1038/s41598-018-26585-0 29802298 6. Jiang L. Li J. Huang K. Li S. Wang Q. Sun Z. Mei T. Wang J. Zhang L. Wang N. Low-Temperature and Solution-Processable Zinc Oxide Transistors for Transparent Electronics ACS Omega 2017 2 8990 8996 10.1021/acsomega.7b01420 31457423 7. Kim Y.M. Moon H.C. Ionoskins: Non-volatile, Highly Transparent, Ultra-Stretchable Ionic Sensory Platforms for Wearable Electronics Adv. Funct. Mater. 2020 30 1907290 10.1002/adfm.201907290 8. Yan Q. Gao L. Tang J. Liu H. Flexible and Stretchable Photodetectors and Gas Sensors for Wearable Healthcare based on Solution-Processable Metal Chalcogenides J. Semicond. 2019 40 111604 10.1088/1674-4926/40/11/111604 9. Kim S. Le T.-H. Park C.S. Park G. Kim K.H. Kim S. Kwon O.S. Lim G.T. Yoon H. A Solution-Processable, Nanostructured, and Conductive Graphene/Polyaniline Hybrid Coating for Metal-Corrosion Protection and Monitoring Sci. Rep. 2017 7 15184 10.1038/s41598-017-15552-w 29123206 10. Liang H.-L. Bay M.M. Vadrucci R. Barty-King C.H. Peng J. Baumberg J.J. Volder M.F.L.D. Vignolini S. Roll-to-Roll Fabrication of Touch-Responsive Cellulose Photonic Laminates Nat. Commun. 2018 9 4632 10.1038/s41467-018-07048-6 30401803 11. Tong S. Yuan J. Zhang C. Wang C. Liu B. Shen J. Xia H. Zou Y. Xie H. Sun J. Large-scale Roll-to-roll Printed, Flexible and Stable Organic Bulk Heterojunction Photodetector NPJ Flex. Electron. 2018 2 7 10.1038/s41528-017-0020-y 12. Espinosa N. Dam H.F. Tanenbaum D.M. Andreasen J.W. Jørgensen M. Krebs F.C. Roll-to-Roll Processing of Inverted Polymer Solar Cells using Hydrated Vanadium (V) Oxide as a PEDOT:PSS Replacement Materials 2011 4 169 182 10.3390/ma4010169 28879984 13. Polat E.O. Balcı O. Kocabas C. Graphene based Flexible Electrochromic Devices Sci. Rep. 2015 4 6484 10.1038/srep06484 25270391 14. Zhang S. Chen S. Hu F. Xu R. Yan B. Jiang M. Gu Y. Yang F. Cao Y. Spray-Processable, Large-Area, Patterned and All-Solid-State Electrochromic Device based on Silica/Polyaniline Nanocomposites Sol. Energy Mater. Sol. Cells 2019 200 109951 10.1016/j.solmat.2019.109951 15. Bellingham A. Bromhead N. Fontecchio A. Rapid Prototyping of Slot Die Devices for Roll to Roll Production of EL Fibers Materials 2017 10 594 10.3390/ma10060594 16. Zhang Z. Guo K. Li Y. Li X. Guan G. Li H. Luo Y. Zhao F. Zhang Q. Wei B. A Colour-Tunable, Weavable Fibre-Shaped Polymer Light-Emitting Electrochemical Cell Nature 2015 9 1 31 10.1038/nphoton.2015.37 17. Chernova N.A. Roppolo M. Dillon A.C. Whittingham M.S. Layered Vanadium and Molybdenum Oxides: Batteries and Electrochromics J. Mater. Chem. 2009 19 2526 2552 10.1039/b819629j 18. Deb S.K. Opportunities and challenges in science and technology of WO3 for electrochromic and related applications Sol. Energy Mater. Sol. Cells 2008 92 245 258 10.1016/j.solmat.2007.01.026 19. Moon H.C. Kim C.-H. Lodge T.P. Frisbie C.D. Multicolored, Low Power, Flexible Electrochromic Devices Based on Ion Gels ACS Appl. Mater. Interfaces 2016 8 6252 6260 10.1021/acsami.6b01307 26867428 20. Kao S.-Y. Kawahara Y. Nakatsuji S. Ho K.-C. Achieving a Large Contrast, Low Driving Voltage, and High Stability Electrochromic Device with a Viologen Chromophore J. Mater. Chem. C 2015 3 3266 3272 10.1039/C5TC00456J 21. Wang X. Guo L. Cao S. Zhao W. Highly Stable Viologens-Based Electrochromic Devices with Low Operational Voltages Utilizing Polymeric Ionic Liquids Chem. Phys. Lett. 2020 749 137434 10.1016/j.cplett.2020.137434 22. Li G. Zhang B. Wang J. Zhao H. Ma W. Xu L. Zhang W. Zhou K. Du Y. He G. Electrochromic Poly(chalcogenoviologen)s as Anode Materials for High-Performance Organic Radical Lithium-Ion Batteries Angew. Chem. 2019 58 8468 8473 10.1002/anie.201903152 30951238 23. Kim J.-W. Myoung J.-M. Flexible and Transparent Electrochromic Displays with Simultaneously Implementable Subpixelated Ion Gel-Based Viologens by Multiple Patterning Adv. Funct. Mater. 2019 29 1808911 10.1002/adfm.201808911 24. Kao S.-Y. Lu H.-C. Kung C.-W. Chen H.-W. Chang T.-H. Ho K.-C. Thermally Cured Dual Functional Viologen-Based All-in-One Electrochromic Devices with Panchromic Modulation ACS Appl. Mater. Interfaces 2016 8 4175 4184 10.1021/acsami.5b11947 26807824 25. Sydam R. Deepa M. Joshi A.G. A Novel 1,1′-bis[4-(5,6-dimethyl-1H -benzimidazole-1-yl)butyl]-4,4′-bipyridinium dibromide (Viologen) for a High Contrast Electrochromic Device Org. Eletcon. 2013 14 1027 1036 10.1016/j.orgel.2013.01.035 26. Li R. Li K. Wang G. Li L. Zhang Q. Yan J. Chen Y. Zhang Q. Hou C. Li Y. Ion-Transport Design for High-Performance Na+ -Based Electrochromics ACS Nano 2018 12 3759 3768 10.1021/acsnano.8b00974 29595953 27. Mortimer R.J. Organic Electrochromic Materials Electrochim. Acta 1999 44 2971 2981 10.1016/S0013-4686(99)00046-8 28. Roy S. Chakraborty C. Nanostructured Metallo-Supramolecular Polymer-based Gel-type Electrochromic Devices with Ultrafast Switching Time and High Colouration Efficiency J. Mater. Chem. C 2019 7 2871 2879 10.1039/C8TC06138F 29. Han F.S. Higuchi M. Kurth D.G. Metallo-Supramolecular Polymers Based on Functionalized Bis-terpyridines as Novel Electrochromic Materials Adv. Mater. 2007 19 3928 3931 10.1002/adma.200700931 30. Higuchi M. Kurth D.G. Electrochemical functions of metallosupramolecular nanomaterials Chem. Rec. 2007 7 203 209 10.1002/tcr.20118 17663446 31. Han F.S. Higuchi M. Kurth D.G. Metallosupramolecular Polyelectrolytes Self-Assembled from Various Pyridine Ring-Substituted Bisterpyridines and Metal Ions: Photophysical, Electrochemical, and Electrochromic Properties J. Am. Chem. Soc. 2008 130 2073 2081 10.1021/ja710380a 18201093 32. Honda K. Fujita M. Ishida H. Yamamoto R. Ohgaki K. Solid-State Electrochromic Devices Composed of Prussian Blue, WO3 , and Poly (ethylene oxide)-Polysiloxane Hybrid-Type Ionic Conducting Membrane J. Electrochem. Soc. 1988 135 3151 3154 10.1149/1.2095519 33. Jiang M. Zhao Z.F. Novel Stable Electrochromic Thin Film: A Prussian Blue Analogue based on Palladium Hexacyanoferrate J. Electroanal. Chem. 1990 292 281 287 10.1016/0022-0728(90)87343-I 34. Shirota Y. Organic materials for electronic and optoelectronic devices J. Mater. Chem. 2000 10 1 25 10.1039/a908130e 35. Heuer H.W. Wehrmann R. Kirchmeyer S. Electrochromic Window Based on Conducting Poly(3,4-ethylenedioxythiophene)–Poly(styrene sulfonate) Adv. Funct. Mater. 2002 12 89 94 10.1002/1616-3028(20020201)12:2<89::AID-ADFM89>3.0.CO;2-1 36. Li X. Yun T.Y. Kim K.-W. Kim S.H. Moon H.C. Voltage-Tunable Dual Image of Electrostatic Force-Assisted Dispensing Printed, Tungsten Trioxide-Based Electrochromic Devices with a Symmetric Configuration ACS Appl. Mater. Interfaces 2020 12 4022 4030 10.1021/acsami.9b21254 31880422 37. Jensen J. Dam H.F. Reynolds J.R. Dyer A.L. Krebs F.C. Manufacture and Demonstration of Organic Photovoltaic-Powered Electrochromic Displays using Roll Coating Methods and Printable Electrolytes J. Polym. Sci. B Polym. Phys. 2012 50 536 545 10.1002/polb.23038 38. Liu H.-S. Chang W.-C. Chou C.-Y. Pan B.-C. Chou Y.-S. Liou G.-S. Liu C.-L. Controllable Electrochromic Polyamide Film and Device Produced by Facile Ultrasonic Spray-coating Sci. Rep. 2017 7 11982 10.1038/s41598-017-11862-1 28931845 39. Cai G.F. Cui M.Q. Kumar V. Darmawan P. Wang J.X. Wang X. Eh A.L.-S. Qian K. Lee P.S. Ultra-large Optical Modulation of Electrochromic Porous WO3 film and the Local Monitoring of Redox Activity Chem. Sci. 2016 7 1373 1382 10.1039/C5SC03727A 29910894 40. Layani M. Darmawan P. Foo W.L. Liu L. Kamyshny A. Mandler D. Magdassi S. Lee P.S. Nanostructured Electrochromic films by Inkjet Printing on Large Area and Flexible Transparent Silver Electrodes Nanoscale 2014 6 4572 4576 10.1039/c3nr06890k 24676234