==== Front Sci Rep Sci Rep Scientific Reports 2045-2322 Nature Publishing Group UK London 37243 10.1038/s41598-023-37243-5 Article Preparation 2-hydroxy-1-naphthaldehyde cross-linked Fe3O4@chitosan-polyacrylamide nanocomposite for removal of everzol black from aqueous solutions Saadat Afshin saadat@iaugermi.ac.ir 1 Banaei Alireza 2 Sattarifar Mehdi 2 Pargolghasemi Parinaz 2 1 Department of Chemistry, Germi Branch, Islamic Azad University, Germi, Iran 2 grid.412462.7 0000 0000 8810 3346 Department of Chemistry, Payame Noor University, P.O. Box 19395-3697, Tehran, Iran 30 6 2023 30 6 2023 2023 13 1061827 3 2023 19 6 2023 © The Author(s) 2023 https://creativecommons.org/licenses/by/4.0/ Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/. In this study, new 2-hydroxy-1-naphthaldehyde linked Fe3O4/chitosan-polyacrylamide nanocomposite (Fe3O4@CS@Am@Nph) were prepared. The synthesized nanocomposite was characterized by (FT-IR), X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), vibrating Sample Magnetometry (VSM) and Termogravimetric Analysis (TGA). The 2-hydroxy-1-naphthaldehyde modified Fe3O4@CS@Am@Nph nanocomposite was used as an effective adsorbent for removal of everzol black from aqueous solutions by batch adsorption procedure. The effects of important parameters on the surface absorption process of everzol black dye, including pH, contact time, adsorbent dosage and initial dye concentration were studied. The Langmuir, Freundlich and Temkin adsorption models were used to describe adsorption isotherms and constants. The equilibrium results revealed that the adsorption behavior of the everzol black dye on the Fe3O4@CS@Am@Nph nanocomposite fitted well with the Langmuir model. On the basis of the Langmuir analysis, the maximum adsorption capacity (qm) of the Fe3O4@CS@Am@Nph for everzol black was found to be 63.69 mg/g. The kinetic studies indicated that adsorption in all cases to be a pseudo second-order process. Further, the thermodynamic studies showed the adsorption to be a spontaneous and endothermic process. Subject terms Chemistry Inorganic chemistry Materials chemistry issue-copyright-statement© Springer Nature Limited 2023 ==== Body pmcIntroduction The extreme use of colorant substances by industries for decades led to the decline of water bodies in the world1,2. For example, industries related dyeing, plasticization and paper making use a lot of water and chemicals to color the products and consequently, they produce a large amount of colored wastewater, which if they are not treated before entering the environment and waters, they will cause many problems. These problems include disrupting the photosynthesis of waters and ecosystems3. Moreover, their complex molecular structure and aromatic rings are toxic and carcinogenic, which can affect human health, water microorganisms, and the environment4,5. Nanofiltration membranes6, ion exchange7, electrochemical oxidation8, photo-catalytic degradation9 and adsorption are methods that have been used to remove colors and pollutants from wastewater. However, most of the above mentioned methods are ineffective due to the factors such as operational costs, secondary wastes, environmental effects and related problems, efficiency and applications10. Among these methods, adsorption is more superior than other methods due to the low initial cost, easy design, suitable flexibility and high efficiency11. In this field, many absorbents including activated carbon, nanoclays, plant biomass and natural absorbents have been used and reviewed12. Among these absorbents, activated carbon is the most suitable absorbent to remove all kinds of pollutants. However, the high price, lack of recycling and reusing have limited the application of this absorbent13. Recently, magnetic nanoparticles have attracted much attentions because they have great magnetic properties such as large surface area, low toxicity, chemical stability, good biocompatibility and biodegradation14,15. It can also be separated from aqueous solutions easily and quickly by using an external magnetic field without requiring tedious filtration or centrifugation16. Chemical or physical change of the surface Fe3O4 nanoparticles with some surfactants or polymers is required for improving the adsorption performance of Fe3O4 nanoparticles17.polysaccharides such as chitosan and its derivatives are more interesting, since the use of chitosan based adsorbents is one of the best ways to remove the colors and ions of heavy metals even at low concentrations18. Chitosan mainly contains poly2-deoxy-d-glucose which is a biopolymer derivative and has well known polymer properties. It has attracted scientist’s attentions because of biocompatibility, biodegradability and nontoxic properties19–22. Because chitosan contains high amounts of amine and hydroxyl groups, it has a very high absorption ability to remove many types of metals such as copper, chromium, silver and platinum. However, in order to improve the absorption properties of adsorbents, much attentions have been paid to the design and synthesis of new adsorbents. For example, magnetic chitosan complex coated on the surface Fe2O3 has been used for removing alizarin red from water environments23. Wang et al. employed magnetic polydopamine-chitosan nanoparticles as adsorption material for the removal of Methylene blue and Malachite green from aqueous solutions24. Zhu et al. synthesized the chitosan-modified magnetic graphitized multi-walled carbon nanotubes for the effective removal of Congo red from aqueous solution25. Armagan et al. performed a comprehensive study on the removal of everzol black by Zeolite26. In this study, new 2-hydroxy-1-naphthaldehyde linked Fe3O4/chitosan-polyacrylamide nanocomposite was synthesized (Fig. 1). The nanocomposite prepared was applied for the removal of the Everzol black from aqueous solution. Moreover, the effects of various parameters such as pH, adsorbent dosage, initial dye concentration and contact time on adsorption behavior were studied. Adsorption isotherms, kinetics and thermodynamic studies have been reported to account for the nature of adsorption process.Figure 1 The synthesis route of Fe3O4@CS@Am@Nph nanocomposite. Results and discussion Preparation of Fe3O4@CS@Am@Nph nanocomposite In the present study, for the preparation of Fe3O4@CS@Am@Nph nanocomposite two-step method was successfully used. In the first step, the Fe3O4@CS@Am nanoparticles were prepared by reaction of Fe3O4 nanoparticles, chitosan and Potassium persulfate. In the second step, Fe3O4@CS@Am nanoparticles were connected on the surface of 2-hydroxy-1-naphthaldehyde by the formation of a Schiff base bond between the amine groups of chitosan and the carbonyl group of 2-hydroxy-1-naphthaldehyde. The synthesis route of Fe3O4@CS@Am@Nph adsorbent are shown in Fig. 1. FT-IR analysis FT-IR spectra of Fe2O3, chitosan, acrylamide, Fe3O4@CS@Am and Fe3O4@CS@Am@Nph are shown in Fig. 2. The characteristic peaks (blue line) of the Fe2O3 appeared at 582 and 628 cm−1 corresponding to Fe–O stretching vibration 1628 and 3426 cm−1 and the peaks at 1628 and 3426 cm−1 assigned to OH bending vibration of Fe2O3 respectively27. For chitosan (red line), a broad band around 3425 cm−1 belongs to amino (NH2) and hydroxyl (OH) groups. Beside the peaks at 2916 and 1381 cm−1 assign to C–H and C–N respectively28. The FTIR spectra of acrylamide (green line) demonstrated absorption peak at 1674 cm−1 showed the presence of C=O group of amides29, also the peaks at 3352, 3192 and 2812 cm−1 attributed to N–H and C–H stretching vibration respectively. The spectrum of Fe3O4@CS@Am (Fig. 2d) showed broader band at 3442 cm−1 which belonged to O–H stretching vibration. Furthermore, the peaks appearing at 2916 cm−1 and 2879 cm−1 belonged to C–H stretching of the alkyl group. This spectrum also showed that the peaks 1662, 1598 and 565 cm−1 are attributed C=O (amide), N–H and Fe–O bands, respectively. The FT-IR spectrum of the Fe3O4@CS@Am@Nph (Fig. 2e) showed a peak at 1627 cm−1 resulted from C=N vibration, which can be due to the of the formed Schiff base between the remained free amino groups of chitosan and 2-hydroxy-1-naphthaldehyde.Figure 2 FT-IR spectra of (a) Fe3O4, (b) Chitosan, (c) Acrylamide, (d) Fe3O4@CS@Am, (e) Fe3O4@CS@Am@Nph. XRD analysis X-ray diffraction of chitosan, Fe3O4 nanoparticles and Fe3O4@CS@Am@Nph nanocomposite particles are shown in Fig. 3. The characteristic XRD peaks for Fe3O4@CS@Am@Nph observed at 2θ = 30.3° (220), 35.6° (311), 43.5° (400), 53.5° (422), 57.3° (511) and 62.5° (440) belong Fe3O4 nanoparticles. Beside the peaks at 2θ = 20° are related to chitosan structure30–32. The average size of Fe3O4@CS@Am@Nph nanocomposite particles is also estimated via Debye–Scherer equation:D=Kλβcosθ, where D is the average size, λ is the X-ray source wavelength (1.54 Å), β is the full width at half maximum (FWHM) of the diffraction peak and θ is the Bragg’s angle.Figure 3 XRD pattern of (a) Chitosan, (b) Fe3O4 and (c) Fe3O4@CS@Am@Nph nanocomposite. According to the Debye–Scherrer equation, the particles size of the Fe3O4@CS@Am@Nph nanocomposite was 193 nm. SEM analysis Scanning electron microscopy (SEM) is used to characterize the morphology and size of Fe3O4, Fe3O4@CS@Am and Fe3O4@CS@Am@Nph nanocomposite. As shown in Fig. 4 the morphology of nanoparticles obtained nearly spherical shape. Furthermore, the size of Fe3O4, Fe3O4@CS@Am and Fe3O4@CS@Am@Nph nanocomposite are relatively uniform and the average diameter are 26–32, 107–165 and 155–173 nm respectively.Figure 4 SEM images of (a) Fe3O4, (b) Fe3O4@CS@Am and (c) Fe3O4@CS@Am@Nph nanocomposite. TGA analysis The TGA curve of the Fe3O4@CS@Am is shown in Fig. S.1. The TGA of the Fe3O4@CS@Am displayed three stages of weight loss between 26 and 600 °C. The first stage decomposition occurred between 26 and 230 °C with 10% corresponds to the adsorbed and bound water in the sample33. The second stage of weight loss was observed in the temperature ranges of 230–315 °C associated with weight loss 31% is related to the heat decomposition of chitosan structure. And the loss 43% in the range from 315 to 580 °C in the third stage is attributed to the decomposition of cross-linked chains of polyacrylamide. About 16% of the sample retained at 600 °C attributed to the existence of Fe3O4 nanoparticles. Furthermore, the TGA of the Fe3O4@CS@Am@Nph nanocomposite (Fig. S.2) showed three stages of weight loss between 26 and 600 °C. The first stage decomposition occurred between 30 and 23 °C with 11% assigned to the adsorbed water in the sample. In two and third stage between 226 and 600 °C weight loss 77% was observed which is attributed to the decomposition of the anchored organic polymers of the adsorbent. The content of Fe3O4 nanoparticles in the nanocomposite is about 12%. Brunauere–Emmette–Teller (BET) The BET analysis was used to determine the surface area, pore size, and pore volume of the Fe3O4@CS@Am@Nph nanocomposite. Figure S.2 represents the BET nitrogen adsorption/desorption isotherm curve of the Fe3O4@CS@Am@Nph nanocomposite. The surface area, pore volume and pore diameter were found to be 9.47 (m2/g), 0.031 (cm3/g) and 13.23 nm respectively for Fe3O4@CS@Am@Nph nanocomposite. The isotherm curve closely matches to a typical type V isotherm graph confirming the mesoporous property of the nanocomposite34. Magnetization analysis The magnetic moment of the prepared Fe3O4@CS@Am@Nph nanocomposite was measured over a range of applied fields between 10,000 and − 10,000 Oe. The magnetization curves of the Fe3O4, Fe3O4@CS@Am and Fe3O4@CS@Am@Nph at room temperature are shown in Fig. 5. The VSM results indicate coating the surface of the magnetite nanoparticles with acrylamide, chitosan and 2-hydroxy-1-naphthaldehyde leads to a decrease in the saturation magnetization. This is due to the presence of acrylamide, chitosan and 2-hydroxy-1-naphthaldehyde on the surface of Fe3O4 nanoparticles which may generate a magnetically dead layer so any crystalline disorder within the surface layer cause to a significant decrease in the saturation magnetization of nanoparticles35. The saturation magnetization values for the Fe3O4 particles, Fe3O4@CS@Am and Fe3O4@CS@Am@Nph nanocomposite were 67, 7and 6 emu/g, respectively. Figure 5 Hysteresis loops of (a) Fe3O4, (b) Fe3O4@CS@Am and (c) Fe3O4@CS@Am@Nph nanocomposite at room temperature using VSM. Sorption studies of selected dyes Effect of adsorbent dosage One of the important factors which affects adsorption processes is adsorbent dose since it determines the capacity of adsorbent for a given initial concentration of dye solution36. In this study, the influence of adsorbent dose on adsorption removal of everzol black dye was studied by using different amounts of sorbent (i.e. 20, 40, 60, 80 and 100 mg) in 40 mL of 100 mg/L solution of dye at 25 °C for 10 min. Figure 6a showed effect of adsorbent dosage on the percentage removal of dye. The results showed that the percent sorption of the everzol black dye increased by increasing the dosage of adsorbent. With the increase in dosage of Fe3O4@CS@Am@Nph nanocomposite, the percentage removal of everzol black dye increased from 58.25 to 94.87. Percentage removal increase can be related to the increased surface area of the adsorbent and availability of more adsorption sites. Therefore, 60 mg adsorbent dosage was chosen for the further experiments.Figure 6 Effect of adsorbent dose (a), initial dye concentration (b), contact time (c) and pH solution (d) on removal of everzol black dye by Fe3O4@CS@Am@Nph (200 rpm, 25 °C). Effect of initial dye concentration The Effect of initial concentration of everzol black on adsorption of it on Fe3O4@CS@Am@Nph nanocomposite were studied in different initial concentrations of dye between 10 and 100 mg/L with keeping constant the other parameters. As result of Fig. 6b illustrates, the percent of dye removal decreases with increase in dye initial concentration from 10 to 100 mg/L. This may be due to the increase of enough number of active sites of dye molecules for binding on the surface of the adsorbent. The percentage removal of everzol black decreases from 93.2 to 25.4%. Effect of contact time The effect of contact time on adsorption of everzol black the surface of Fe3O4@CS@Am@Nph nanocomposite were studied at room temperature with the different contacting time at 10 and 20 min. As it can be seen in Fig. 6c, by increasing the contact time percent adsorption of everzol black on Fe3O4@CS@Am@Nph was increased. Effect of initial pH solution The pH plays a crucial role in the adsorption of dye onto the adsorbent. Indeed, the pH affects the adsorption process through the degree of ionization, the surface charge of the adsorbent, or the speciation of the adsorbate. In this study, the effect of initial pH on the sorption of everzol black onto Fe3O4@CS@Am@Nph nanocomposite were studied at different values from 2 to 12. For this experiment, 0.1 M NaOH and 0.1 M HCl solutions were used to adjust the pH of the solution. The effect of pH on the percentage removal of everzol black by Fe3O4@CS@Am@Nph is shown in Fig. 6d. In acidic conditions the amount of adsorption is increased that can be due to electrostatic attraction between positive charge of amino groups of chitosan and negative charge of sulfonate groups of the everzol black dye. Adsorption isotherms Adsorption isotherm is a method to investigate the relationship between the adsorbed amount in the liquid phase on adsorbent in equilibrium and constant temperature37. In fact, the adsorption isotherm describes the interaction between the adsorbent and adsorbed surfaces. Therefore, it is always considered as a fundamental factor for determining the absorbent capacity and optimizing the absorbents38. In the present study, Langmuir, Freundlich and Temkin isotherm models were used to obtain the isotherm parameters for adsorption of everzol black onto Fe3O4@CS@Am@Nph nanocomposite. Investigating the experimental data obtained from adsorption in equilibrium with theoretical models and obtaining the relationship between them provides important information for the best possible design of an absorbent system. Langmuir adsorption isotherm: In this model, there is no interaction among adsorbed molecules and adsorption process happens on homogeneous surfaces, showed in below Eq. (1)39:1 Ceqe=1KL·qm+Ceqm, where, Ce is the equilibrium concentration of the dye solution (mg/L), qe (mg/g) is the amount of dye adsorbed, qm is the value of monolayer adsorption capacity in Langmuir model and KL: constant value of Langmuir (mg/L). The Langmuir plot for the adsorption of everzol black onto Fe3O4@CS@Am@Nph nanocomposite at different temperatures is shown in Fig. 7.Figure 7 Langmuir plot for the adsorption of everzol black (200 rpm, 25 °C and pH 7). Freundlich isotherm model (2) is the more for the adsorption of components dissolved in a liquid solution, it is assumed that: First, the adsorption is monolayer and chemical, and second, the energy of the adsorption sites is not the same, i.e. the adsorbent surface is not uniform40:2 Lnqe=LnKf+1nLnCe. KF and n are experimental constants where KF is adsorption capacity at unit concentration (L/mg) and n shows the intensity of adsorption. The 1/n values can be classified as irreversible (1/n = 0), favorable (0 < 1/n < 1) and unfavorable (1/n > 1). Calculation of KF and n in Freundlich model for Fe3O4@CS@Am@Nph nanocomposite shown in Fig. 8. Also, the separation factor (RL) was calculated by the following Eq. (3):Figure 8 Freundlich plot for the adsorption of everzol black (200 rpm, 25 °C and pH 7). 3 RL=11+KL·C0. The values of RL can illustrate the shape of the isotherm to be either unfavorable (RL > 1), linear (RL = 1), favorable (0 < RL < 1) or irreversible (RL = 0). The values of Langmuir and Freundlich parameters and the regression coefficients R2 of the adsorption of everzol black onto Fe3O4@CS@Am@Nph are given in Table S.1. According to Table S.1, the value of RL was obtained in the range of 0 < RL < 1, that showed adsorption of the everzol black on Fe3O4@CS@Am@Nph was favorable. The maximum monolayer adsorption capacity (qm) calculated by Langmuir model was found to be 63.69 and regression coefficient value is 0.9959. Temkin adsorption isotherm directly takes into account of adsorbent-adsorbate interactions. The Temkin isotherm equation is:4 qe=BlnA+BlnCe, 5 B=RTb, where R is gas constant 8.314 J/mol/K. T is absolute temperature (K), b is the Temkin constant related to the heat of adsorption (J/mol) and A is the equilibrium binding constant corresponding to the maximum binding energy (L/g). The linear plot (Fig. 9) of qe versus lnCe enable to determine the constant A and b. The values of Temkin parameters and the regression coefficients R2 of the adsorption of everzol black onto Fe3O4@CS@Am@Nph are given in Table S.1.Figure 9 Temkin plot for the adsorption of everzol black (200 rpm, 25 °C and pH 7). Adsorption kinetics In order to determine the type of adsorption kinetics pseudo-first-order41 and pseudo-second-order42 kinetics were investigated for the Fe3O4@CS@Am@Nph nanocomposite. The linear equation of pseudo-first-order and pseudo-second-order kinetic are given by Eqs. (6) and (7), respectively:6 logqe-qt=logqe-K12.303t, 7 tqt=1K2qe2+tqe, where qe and qt (mg/g) is the amount of dye adsorbed at equilibrium and at time t, K1 and K2 (min−1) are the rate constants. Figure 10 shows the absorption kinetics using different models. In the pseudo-first-order model, the values of rate constant k1 and qe are calculated from the straight line plots of log(qe–qt) vs time (Fig. 10a). The values of first order rate constant (k1), amount of dye adsorbed at equilibrium (qe) and coefficient of linear regression (R2) were obtained 0.012 min−1, 28.8 (mg/g) and 0.9566, respectively. As it is shown in the Fig. 10b pseudo-second-order constants can be calculated from the linear plot between t/qt and time. The values of k2, qe and R2 were obtained 0.0094/min, 33.22 (mg/g) and 0.9918, respectively. The qe value obtained by calculating pseudo second order kinetic is close to the experimental value (49.73), also the pseudo second order model has high regression coefficient (R2 = 0.9918) than the pseudo first order (R2 = 0.9566).Figure 10 Pseudo-first-order (a) and Pseudo-Second-order (b) model for the removal kinetics of everzol black on Fe3O4@CS@Am@Nph nanocomposite (50 mg/L, 25 °C and pH 7). Thermodynamic studies In order to investigate the thermodynamics of adsorption, important parameters such as entropy change (ΔS), enthalpy change (ΔH) and standard Gibbs free energy change (ΔG) on the adsorbent at different temperatures (283, 293 and 308 K) were investigated for surface adsorption of everzol black dye. The values of thermodynamic relations of adsorption were calculated using the following equations:8 LnKL=ΔS∘R-ΔH∘RT, 9 ΔG∘=ΔH∘-TΔS∘, where KL is the Langmuir constant (L/mol), T is the solution temperature and R is the universal gas constant (8.314 J/mol K). The values of enthalpy changes of adsorption (ΔH∘) and entropy changes (ΔS∘) were determined from slope and intercept of plot Ln KL vs 1/T (Fig. 11). Table S.2 shows the thermodynamic parameters for the adsorption of everzol black on Fe3O4@CS@Am@Nph nanocomposite. The positive value of ΔH∘ shows that the adsorption of everzol black on Fe3O4@CS@Am@Nph nanocomposite is endothermic. The increasing the degree of freedom of the everzol black on the nanocomposite may be its reason. Also, The positive value of ΔS∘ indicate the increased randomness and disorder at the adsorbent-solution interface during the adsorption of dye on Fe3O4@CS@Am@Nph nanocomposite. The negative values of ΔG∘ in different temperatures shows that the adsorption of dye on Fe3O4@CS@Am@Nph nanocomposite is spontaneous process.Figure 11 Thermodynamic plot for removal of everzol black on Fe3O4@CS@Am@Nph nanocomposite. Adsorption mechanism Figure 12 shows mechanism of adsorption of everzol black on Fe3O4@CS@Am@Nph nanocomposite. As seen in Fig. 11, the π–π bond interactions between aromatic rings of dye and 2-hydroxy-1-naphthaldehyde, the electrostatic interactions of negatively charged sulfonate groups of dye and the positively charged protonated amino groups of chitosan and also hydrogen bonding interactions between amine groups and oxygen atom of OH group play important role in adsorption of everzol black on Fe3O4@CS@Am@Nph nanocomposite.Figure 12 Mechanism of everzol black adsorption on Fe3O4@CS@Am@Nph nanocomposite. Reusability studies The reusing of adsorbent is of great importance as a cost effective process in water treatment. The regeneration ability of Fe3O4@CS@Am@Nph sample was evaluated by studying adsorption–desorption process in four cycle. Figure 13 shows the percentage removal of dye in 0.1 M HCl solution. As can be seen from Fig. 13, after 4 successive cycles, the dye removal percentage decreased slightly and was still 71%. This suggested that the Fe3O4@CS@Am@Nph nanocomposite is efficient for everzol black.Figure 13 Regeneration studies for the adsorption–desorption of dye onto Fe3O4@CS@Am@Nph nanocomposite. Comparison with other reported adsorbents The result obtained by comparing this adsorbent with other established adsorbents were shown in Table 1. As Table 1 demonstrates, that the Fe3O4@CS@Am@Nph nanocomposite had an acceptable adsorption capacity for everzol black dye in comparison with other adsorbents. The high adsorption capacity of studied adsorbent reveals that the adsorbent is very effective in the removal of everzol black from aqueous solutions.Table 1 Comparison of the adsorption capacity of present system with other reported systems. Adsorbents Dye qm (mg/g) References ChM nanoparticles Reactive Black 5 50.00 43 ChM GL nanoparticles Reactive Black 5 36.94 43 ChM ECH nanoparticles Reactive Black 5 33.63 43 CS@ZnO-MS nanocomposite Eriochrome Black-T 30.00 44 CS@ZnO-MA nanocomposite Eriochrome Black-T 26.45 44 Fe3O4@CS@Am@Nph nanocomposite Everzol black 63.69 Present study Conclusion In this study, 2-hydroxy-1-naphthaldehyde linked Fe3O4/chitosan-polyacrylamide nanocomposite was prepared. The synthesized nanoparticles were characterized by (FT-IR), XRD, SEM, VSM and TGA. The modified Fe3O4/chitosan-polyacrylamide nanocomposite was used successfully as an effective sorbent for the removal of everzol black dye from aqueous solutions. The effects of various parameters such as adsorbent dose, solution pH, initial dye concentration and contact time on the adsorption process were investigated. The Langmuir, Freundlich and Temkin isotherm models were applied to analyze the experimental data. The maximum adsorption capacity of Fe3O4@CS@Am@Nph for everzol black was 63.69 mg/g at 25 °C. The kinetic studies indicated the adsorption in all cases to be a pseudo second-order process. Further, the thermodynamic studies showed the adsorption to be a spontaneous and endothermic process. Experimental Chemicals and reagents Ferric chloride hexahydrate (FeCl3⋅6H2O) with 98% purity, ferrous chloride tetrahydrate (FeCl3⋅4H2O) with 98% purity, absolute ethanol, 2-hydroxy-1-naphthaldehyde, Chitosan, glycerol with 99% purity and ammonia (NH3) with 25% purity were purchased from Merck, Germany. Everzol Black (chemical formula = C26H21N5Na4O19S6, Molecular weight (g/mol) = 991.82, λmax = 436 nm) was purchased from the Textile Factory. The chemical structure of Everzol Black is shown in Fig. S.3. Instrumentation FT-IR spectra (Shimadzu prestige-21) were used to determine the identity of the as prepared nanoparticles and to characterize the coated Fe3O4 nanoparticles. X-ray powder diffraction measurements were performed using an X-ray diffractometer (XRD) (Perkin Elmer) at ambient temperature. The surface morphology of the silica-supported ligands was identified with a scanning electron microscope (LECO SEM, Michigan, USA). Magnetic measurements were performed by means of the vibrating sample magnetometery method, using a VSM 7407 magnetometer, at room temperature. Thermogravimetric analysis (TGA) was performed using a Perkin Elmer thermogravimetric analyzer. UV–Visible spectra in the 200–1000 nm range were obtained in DMF solvent on a Perkin Elmer Lambda 45 spectrophotometer. A Jenway model 4510 pH-meter was used for pH measurements by use of a combined electrode. An ultrasonication probe (Karl Deutsch, Germany) was used to disperse the nanoparticles in the solution. Preparation of magnetite nanoparticles (Fe3O4) The Fe3O4 nanoparticles were prepared according to Ref.45 with minor modifications. Briefly, FeCl3⋅6H2O (11.68 g) and FeCl2⋅4H2O (4.30 g) were dissolved in 200 mL deionized water under nitrogen gas with vigorous stirring at 85 °C. Then, 20 mL of 30% aqueous ammonia was added to the solution. The color of the bulk solution changed from orange to black immediately. The magnetic precipitates were washed twice with deionized water and once with 0.02 mol/L sodium chloride. The washed magnetite was stored in deionized water at a concentration of 40 g/L. Preparation of Fe3O4@CS@Am nanocomposite To a suspension of the Fe3O4 nanoparticles (0.35 g) in DI water/methanol (100 mL), chitosan (CS) (2 g) and acrylamide (1 g) were added. The mixed solution was ultrasonically dispersed for 30 min. The polymerization reaction of acrylamide was initiated by K2S2O8 (0.04 g), and the reaction was allowed to proceed for 12 h at 80 °C under nitrogen atmosphere and mechanical stirring. The resulting solid was magnetically separated, washed with water/methanol several times to remove the unreacted ligands and dried under vacuum. Preparation of Fe3O4@CS@Am@Nph nanocomposite To a suspension of the Fe3O4@CS@Am nanoparticles (1 g) in ethanol (150 mL), 2-hydroxy-1-naphthaldehyde (Nph) was added (0.5 g). The reaction mixture was refluxed for 48 h under nitrogen atmosphere. The Fe3O4@CS@Am@Nph nanocomposite were separated by an external magnet, washed with distilled water and ethanol then dried in vacuum at 60 °C for 24 h. Adsorption experiments Synthesized nanoparticles were used removal of everzol black dye from aqueous solutions. Various parameters such as initial concentration, contact time, adsorbent dose and pH on adsorption were studied. For performing the experiments, solution of 1000 mg/L of everzol black was prepared in deionized water and diluted to obtain the desired concentrations of dye. Different amounts of nanoparticles, varying from 20 to 100 mg, was suspended in a series of 40 mL dye solution with concentrations varying from 40 to 120 mg/L using 50 mL glass flasks. For suitable times from 10 to 20 min the suspensions were stirred and also the effect of solution pH on dye removal was investigated through adjusting by 0.01 N HCl or NaOH solutions. The nanoparticles adsorbent was separated from aqueous solution by an external magnetic field. The concentration of the everzol black was analyzed by UV-spectrophotometer at λmax 600 nm. The amount of the dye adsorbed onto adsorbent (qe in mg/g) and the percentage of the dyes removed from the solution (R in %) were calculated from the equations:10 qe=(C0-Ce)M×V, 11 \%R=(C0-Ce)C0×100, where, C0 and Ce are the initial and equilibrium concentration of dye in solution (mg/L), respectively. V is the initial volume of the dye solution (L) and M is the mass of adsorbent used (g). Reusability studies For the reusing possibility study, 20 mg of Fe3O4@CS@Am@Nph nanocomposite was added to the solution containing 25 mL of 100 mg/L dye for 30 min under 200 rpm at 298 K. The sample was filtered, and dye saturated Fe3O4@CS@Am@Nph sample was treated with of 0.1 M HCl. The percentage of desorption (D) was calculated using the equation:12 D=Amount of dye desorbedAmount of dye adsorbed×100. Supplementary Information Supplementary Information. Supplementary Information The online version contains supplementary material available at 10.1038/s41598-023-37243-5. Author contributions All of us prepared manuscript collaboratively. Data availability All data supporting the conclusions of this research article are included within the manuscript. Competing interests The authors declare no competing interests. Publisher's note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations. ==== Refs References 1. Farhan Hanafi M Sapawe N A review on the water problem associate with organic pollutants derived from phenol, methyl orange, and remazol brilliant blue dyes Mater. Today Proc. 2020 31 A141 A150 10.1016/j.matpr.2021.01.258 2. Velusamy S Roy A Sundaram S Kumar Mallick T A review on heavy metal ions and containing dyes removal through graphene oxide-based adsorption strategies for textile wastewater treatment Chem. Rec. 2021 21 1570 1610 10.1002/tcr.202000153 33539046 3. Bashir I Lone FA Bhat RA Mir SA Dar ZA Dar SA Concerns and threats of contamination on aquatic ecosystems Bioremediat. Biotechnol. 2020 27 1 26 4. Oussalah A Boukerroui A Aichour A Djellouli B Cationic and anionic dyes removal by low-cost hybrid alginate/natural bentonite composite beads: Adsorption and reusability studies Int. J. Biol. Macromol. 2019 124 854 862 10.1016/j.ijbiomac.2018.11.197 30471398 5. Carneiro PA Umbuzeiro GA Oliveira DP Zanoni MVB Assessment of water contamination caused by a mutagenic textile effluent/dyehouse effluent bearing disperse dyes J. Hazard. Mater. 2010 174 694 699 10.1016/j.jhazmat.2009.09.106 19853375 6. Cao Y Chen X Feng Sh Wan Y Luo J Nanofiltration for decolorization: Membrane fabrication, applications and challenges Ind. Eng. Chem. Res. 2020 59 19858 19875 10.1021/acs.iecr.0c04277 7. El Ouardi Y Virolainen S MassimaMouele ES Laatikainen M Repo E Laatikainen K The recent progress of ion exchange for the separation of rare earths from secondary resources Hydrometallurgy 2023 2018 106047 10.1016/j.hydromet.2023.106047 8. Liu N Wu Y Removal of methylene blue by electrocoagulation: A study of the effect of operational parameters and mechanism Ionics 2019 25 3953 3960 10.1007/s11581-019-02915-8 9. Saufi H Alouani M Alehyen S Achouri M Aride J Taibi M Photocatalytic degradation of methylene blue from aqueous medium onto perlite-based geopolymer Int. J. Chem. Eng. 2020 2020 1 7 10.1155/2020/9498349 10. Mulushewa Z Dinbore WT Ayele Y Removal of methylene blue from textile waste water using kaolin and zeolite-x synthesized from Ethiopian kaolin Environ. Anal. Health Toxicol. 2021 36 e2021007 10.5620/eaht.2021007 33765746 11. Li Y Liang YQ Mao XM Li H Efficient removal of Cu(II) from an aqueous solution using a novel chitosan assisted EDTA-intercalated hydrotalcite-like compound composite: Preparation, characterization, and adsorption mechanism Chem. Eng. J. 2022 438 135531 10.1016/j.cej.2022.135531 12. Ismael KK Esther MK Esther WN Cyprian MM Joseph MM Review of clay-based nanocomposites as adsorbents for the removal of heavy metals J. Chem. 2022 2022 1 25 13. Karimi MH Mahdavinia GR Massoumi B Baghban A Saraei M Ionically crosslinked magnetic chitosan/κ-carrageenan bioadsorbents for removal of anionic eriochrome black-T Int. J. Biol. Macromol. 2018 113 361 375 10.1016/j.ijbiomac.2018.02.102 29471096 14. Kulal P Badalamoole V Efficient removal of dyes and heavy metal ions from waste water using Gum ghatti–graft–poly(4-acryloylmorpholine) hydrogel incorporated with magnetite nanoparticles J. Environ. Chem. Eng. 2020 8 104207 10.1016/j.jece.2020.104207 15. Kulal P Vishalakshi B Magnetite nanoparticle embedded Pectin-graft poly(Nhydroxyethylacrylamide) hydrogel: Evaluation as adsorbent for dyes and heavy metal ions from waste water Int. J. Biol. Macromol. 2020 156 1408 1417 10.1016/j.ijbiomac.2019.11.181 31760033 16. Mittal A Roy I Gandhi S Magnetic nanoparticles: An overview for biomedical applications Magnetochemistry 2022 8 107 10.3390/magnetochemistry8090107 17. Oliva FSN Sahihi M Lenglet L Ospina A Guenin E Jaramillo-Botero A Goddard WA Bedoui F Nanoparticle size and surface chemistry effects on mechanical and physical properties of nano-reinforced polymers: The case of PVDF-Fe3O4 nano-composites Polymer Test. 2023 117 107851 10.1016/j.polymertesting.2022.107851 18. Picos-Corrales LA Morales-Burgos AM Ruelas-Leyva JP Crini G García-Armenta Sergio E Jimenez-Lam SA Ayón-Reyna LE Rocha-Alonzo F Calderón-Zamora L Osuna-Martínez U Calderón-Castro A De-Paz-Arroyo G Inzunza-Camacho LN Chitosan as an outstanding polysaccharide improving health-commodities of humans and environmental protection Polymers 2023 15 3 526 10.3390/polym15030526 36771826 19. Piekarska K Sikora M Owczarek M Jóźwik-Pruska J Wiśniewska-Wrona M Chitin and chitosan as polymers of the future-obtaining, modification, life cycle assessment and main directions of application Polymers 2023 15 4 793 10.3390/polym15040793 36850077 20. Chopra L Chohan JS Sharma S Pelc M Kawala-Sterniuk A Multifunctional modified chitosan biopolymers for dual applications in biomedical and industrial field: Synthesis and evaluation of thermal, chemical, morphological, structural, in vitro drug-release rate, swelling and metal uptake studies Sensors 2022 22 9 3454 10.3390/s22093454 35591144 21 Bakshi PS Selvakumar D Kadirvelu K Kumar NS Chitosan as an environment friendly biomaterial—A review on recent modifications and applications Int. J. Biol. Macromol. 2020 150 1072 1083 10.1016/j.ijbiomac.2019.10.113 31739057 22. Lima R Fernandes C Pinto M Molecular modifications, biological activities, and applications of chitosan and derivatives: A recent update Chirality 2022 34 1166 1190 10.1002/chir.23477 35699356 23. Rathinam K Kou X Hobby R Panglisch S Sustainable development of magnetic chitosan core–shell network for the removal of organic dyes from aqueous solutions Materials 2021 14 7701 10.3390/ma14247701 34947299 24. Wang Y Zhang Y Hou CH Liu M Mussel-inspired synthesis of magnetic polydopamine-chitosan nanoparticles as biosorbent for dyes and metals removal J. Taiwan Inst. Chem. Eng. 2016 1 e7 25. Zhu HY Fu YQ Jiang R Yao J Liu L Chen YW Xiao L Zeng GM Preparation, characterization and adsorption properties of chitosan modified magnetic graphitized multi-walled carbon nanotubes for highly effective removal of a carcinogenic dye from aqueous solution Appl. Surf. Sci. 2013 285 865 873 10.1016/j.apsusc.2013.09.003 26. Armagan B Turan M Celik MS Equilibrium studies on the adsorption of reactive azo dyes into zeolite Desalination 2004 170 33 39 10.1016/j.desal.2004.02.091 27. Gupta VK Agarwal S Saleh TA Chromium removal by combining the magnetic properties of iron oxide with adsorption properties of carbon nanotubes Water Res. 2011 45 2207 2212 10.1016/j.watres.2011.01.012 21303713 28. Abou El-Reash YG Magnetic chitosan modified with cysteine-glutaraldehyde as adsorbent for removal of heavy metals from water J. Environ. Chem. Eng. 2016 4 3835 3847 10.1016/j.jece.2016.08.014 29. Karimi M Shojaei A Nematollahzadeh A Abdekhodaie MJ Column study of Cr (VI) adsorption onto modified silica-polyacrylamide microspheres composite Chem. Eng. J. 2012 210 280 288 10.1016/j.cej.2012.08.046 30. Hoque MA Ahmed MR Rahman GT Rahman MT Islam MA Khan MA Hossain MK Fabrication and comparative study of magnetic Fe and α-Fe2O3 nanoparticles dispersed hybrid polymer (PVA+Chitosan) novel nanocomposite film Results Phys. 2018 10 434 443 10.1016/j.rinp.2018.06.010 31. Günister E Pestreli D Ünlü CH Atıcı O Güngör N Synthesis and characterization of chitosan-MMT biocomposite systems Carbohyd. Polym. 2007 67 358 365 10.1016/j.carbpol.2006.06.004 32. Julkapli NM Akil HM X-ray powder diffraction (XRD) studies on Kenaf dust filled chitosan bio-composites, neutron and X-ray scattering Int. Conf. 2008 989 111 114 33. Tanhaei B Ayati A Lahtinen M Sillanpaa M Preparation and characterization of a novel chitosan/Al2O3/magnetite nanoparticles composite adsorbent for kinetic, thermodynamic and isotherm studies of Methyl Orange adsorption Chem. Eng. J. 2015 259 1 10 10.1016/j.cej.2014.07.109 34. Karunakaran G Kundu M Maduraiveeran G Kolesnikov E Gorshenkov MV Balasingam SK Kumari S Sasidharan M Kuznetsov D Hollow mesoporous heterostructures negative electrode comprised of CoFe2O4@ Fe3O4 for next generation lithium ion batteries Microporous Mesoporous Mater. 2018 272 1 7 10.1016/j.micromeso.2018.06.005 35 Gui-yin L Jiang Yu-ren J Huang K Ding P Chen J Preparation and properties of magnetic Fe3O4–chitosan nanoparticles J. Alloys Compds. 2008 466 1–2 451 456 36. Fontana KB Chaves ES Sanchez JDS Watanabe ERLR Pietrobelli JMTA Lenzi GG Textile dye removal from aqueous solutions by malt bagasse: Isotherm, kinetic and thermodynamic studies Ecotoxicol. Environ. Saf. 2016 124 329 336 10.1016/j.ecoenv.2015.11.012 26590694 37. Wawrzkiewicz M Wiśniewska M Gunko VM Zarko VI Adsorptive removal of acid, reactive and direct dyes from aqueous solutions and wastewater using mixed silica–alumina oxide Powder Technol. 2015 278 306 315 10.1016/j.powtec.2015.03.035 38. Tabak A Eren E Afsin B Caglar B Determination of adsorptive properties of a Turkish Sepiolite for removal of Reactive Blue 15 anionic dye from aqueous solutions J. Hazard. Mater. 2009 161 1087 1094 10.1016/j.jhazmat.2008.04.062 18534746 39. Mahmood T Aslam M Naeem A Siddique TU Din S Adsorption of As (III) from aqueous solution onto iron impregnated used tea activated carbon: Equilibrium, kinetic and thermodynamic study J. Chil. Chem. Soc. 2018 63 3855 3866 10.4067/s0717-97072018000103855 40. Aly Z Graulet A Scales N Hanley T Removal of aluminium from aqueous solutions using PAN-based adsorbents: Characterisation, kinetics, equilibrium and thermodynamic studies Environ. Sci. Pollut. Res. 2014 21 3972 3986 10.1007/s11356-013-2305-6 41. Chen SX Wang J Wu ZL Deng Q Tu WF Dai GP Zeng ZL Deng SG Enhanced Cr(VI) removal by polyethylenimine and phosphorus codoped hierarchical porous carbons J. Colloid Interface Sci. 2018 523 110 120 10.1016/j.jcis.2018.03.057 29614420 42. Alqadami AA Naushad M Abdalla MA Khan MR Alothman ZA Adsorptive removal of toxic dye using Fe3O4−TSC nanocomposite: Equilibrium, kinetic and thermodynamic studies J. Chem. Eng. Data 2016 61 3806 3813 10.1021/acs.jced.6b00446 43. Freire TM Fechine LMUD Queiroz DC Freire RM Denardin JC Ricardo NMPS Rodrigues TNB Gondim DR Junior IJS Fechine PBA Magnetic porous controlled Fe3O4–chitosan nanostructure: An ecofriendly adsorbent for efficient removal of azo dyes Nanomaterials 2020 10 1194 10.3390/nano10061194 32575349 44. Raval NP Priyadarshi GV Mukherjee S Zala H Fatma D Bonilla-Petriciolet A Abdelmottaleb BL Duclaux L Trivedi MH Statistical physics modeling and evaluation of adsorption properties of chitosan-zinc oxide nanocomposites for the removal of an anionic dye J. Environ. Chem. Eng. 2022 10 108873 10.1016/j.jece.2022.108873 45. Huang C Hu B Silica-coated magnetic nanoparticles modified with γ-mercaptopropyltrimethoxysilane for fast and selective solid phase extraction of trace amounts of Cd, Cu, Hg, and Pb in environmental and biological samples prior to their determination by inductively coupled plasma mass spectrometry Spectrochim. Acta B 2008 63 437 444 10.1016/j.sab.2007.12.010